【摘 要】
:
以F/U的终摩尔比、F/U的初摩尔比、缩聚阶段pH值、缩聚阶段温度为变量,UF中游离甲醛含量和羟甲基含量为考核指标来设计正交试验,优化脲醛树脂合成工艺参数.最佳工艺参数F/U的
论文部分内容阅读
以F/U的终摩尔比、F/U的初摩尔比、缩聚阶段pH值、缩聚阶段温度为变量,UF中游离甲醛含量和羟甲基含量为考核指标来设计正交试验,优化脲醛树脂合成工艺参数.最佳工艺参数F/U的终摩尔比1.05:1、F/U的初摩尔比2.2:1、缩聚阶段pH值5.1~5.3、缩聚阶段温度88℃~90℃.其产品游离甲醛含量小于0.15%,羟甲基含量大于10.5%.“,”The orthogonal test was designed by the final molar ratio of formaldehyde to urea,initial molar ratio of formaldehyde to urea,pH value and temperature of condensation stage for variable,free-formaldehyde content and hydroxymethyl content of UF resin for examination index.Synthetic processing parameter of urea formaldehyde resin was optimized.The optimal process parameters were that the final molar ratio of formaldehyde to urea was 1.05:1,initial molar ratio of formaldehyde to urea was 2.2:1,pH value was 5.1~5.3 and temperature was 88℃~90℃ of condensation stage.Free-formaldehyde content of UF resin was below0.15% and hydroxymethyl content was over 10.5%.
其他文献
三公司实行真正的项目法施工始于2002年。在2001年以前,公司是以刚性建制的施工队进行施工生产,机械设备相对集中于各施工队,设备维修按照传统管理模式运行;2002年以后,队建
针对黑龙江省森工林区南岔林业局目前的森林资源经营状况,分析了其存在的问题及原因,进而就如何加强该林区森林资源管理、改善林分质量提出建议.“,”To improve the level o
将无水CuCl2、无水AlCl3、无水FeCl3、无水MnCl2,无水MgCl2和无水ZnCl2加入到双酚A-苯胺型聚苯并恶嗪中,通过红外光谱(FTIR),核磁共振氢谱(1H-NMR),热失重分析(TGA)和元素分
论述了黑龙江省方正林业局生态教育示范基地建设的内容与意义,其中包括生态文化林和生态园区的调查设计、作业施工内容、施工要求、管护措施以及效益前景分析.“,”Forest ec
通过多技术油液分析技术,对综合传动装置润滑油液中富含的设备运行状态信息进行提取,利用油液污染度界限值,建立了综合传动磨损故障诊断模型,并依据可靠性寿命试验过程中发生
应我校经济管理学院邀请,中国有色金属工业总公司供销公司副总经理、总公司期货领导小组成员兼办公室主任、著名期货专家张宜生教授于1996年9月中旬来我校与广大师生就“中国
通过对某传动装置的污染源的分析,提出控制液压系统污染的方法,将污染控制系统的设计纳入到系统设计中来,有效的控制系统的污染物的产生。并在使用过程中对其进行监测,做到预
通过走访调查,针对黑龙江省穆棱林业局林地保护利用提出了相关的管理办法和保护利用措施.“,”The author visited the investigation,for forest protection and utilizatio
通过对黑龙江省东方红林业局林地和林木资源的调查研究,并参照国家有关林地保护利用的相关规划要求,对该局的林地保护利用总体方向和落实措施提出建议.“,”This article ref
分析了黑龙江省鹤北林业局的木材加工企业现状,并就目前加工企业存在的问题提出相应解决对策.“,”Analysis to the current situation of wood processing enterprises in H