700 MPa微合金钢(/%:0.05C,0.18Si,1.80Mn,0.010P,0.003S,0.15Mo,0.10Ti,0.75Nb,0.035V,0.030Al,0.002 0Ca)的冶炼工艺为240 t BOF-LF-2150 mm板坯连铸。通过利用金相显微镜、扫描电镜、能谱仪和拉力试验机试验了700 MPa级微合金高强钢轧后,10 mm钢带从600℃卷取时直接取样经3.7 h冷却至室温(25℃)的空冷工艺,和钢带600℃卷取后并堆放在一起经36.2 h缓慢冷却到室温(25℃)的缓冷工艺的组织和