【摘 要】
：
Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18％,manganese content of 12％,15％,18％,and nitro
【机 构】
：
School of Materials Science and Engineering,Materials Science and Engineering Program,School of Meta
论文部分内容阅读
Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18％,manganese content of 12％,15％,18％,and nitrogen content of 0.43％,0.53％,0.67％,respectively.The mechanisms of precipitation and solid solution of high nitrogen austenitic stainless steel were studied using the scanning electron microscopy,transmission electron microscopy,electron probe micro analysis and mechanical testing.The results show that,Cr2N is the primary precipitate in the tested stainless steels instead of Cr23C6- Cr2N nucleates at austenitic grain boundaries and grows towards inner grains with a lamellar morphology.By means of pre-precipitation of Cr2N at 800 ℃,the microstructure of the steels at solid solution state can be refined,thus improving the strength and plasticity.After the proposed treatment,the tensile strength,the proof strength and the elongation of the tested steel reach 881 MPa,542 MPa and 54％,respectively.
其他文献
The element diffusion process of Nb3Sn superconductors by bronze route was studied using X-ray diffraction,scanning electron microscopy and energy dispersive sp
Thermo-plasticity of homogenized 7050 aluminum ingot was investigated by instantaneous tensile tests conducted at different temperatures.The results show that,w
In the present paper,the moment Lyapunov exponent of a codimensional two-bifurcation system is evaluted,which is on a three-dimensional central manifold and sub
To explore the energy saving effect of building envelope,the experiments were carried out through a comparison of basic cubicle in summer.Experiments show that
The reduction of ilmenitc concentrate by hydrogen gas was investigated m the temperature range of 500 to 1200℃.The micro-structure and phase transition of the
(Al65Cu20Fe15)100-xSnx (x=0,12,20,30) and Al57Si10Cu18Fe15 powders were cladded on a medium carbon steel (45# steel) substrate by laser multilayer cladding,resp
Achieving simultaneous reduction of NOx,CO and unburned hydrocarbon (UHC) emissions without compromising engine performance at part loads is the current focus o
In magnetic Czochralski (MCZ) silicon growth,the distance and diameter of the electrified coils may affect the magnetic field intensity and melt flow.By changin
Optical microscopy (OM) and transmission electron microscopy (TEM) were used to investigate the effect of tempering temperature on the experimental extra-high c
This paper demonstrated our discovery of the movement effect of BiFeO3 nanoparticles in solution by strong electrical polarization.First,BiFeO3 nanoparticles we