The positive temperature coefficient resistance ( PTCR) barium titanate ceramic samples have been prepared by the standard solid-state reaction method, and the ceramic samples have been treated by depositing copper films with magnetron sputtering method. The metallic copper films deposited on the ceramic substrates have been mixed at room temperature with argon ions in energy of 400 keV. Ion beam mixing induced modification of PTCR behavior of the ceramics was studied by using the ac complex impedance method and the resistance vs. temperature measurements . The results showed that room temperature resistance dramatically decreased and Curie point shifted toward higher temperature side for the ion beam mixed samples.
The positive temperature coefficient resistance (PTCR) barium titanate ceramic samples have been prepared by the standard solid-state reaction method, and the ceramic samples have been treated by depositing copper films with magnetron sputtering method. The metallic copper films deposited on the ceramic substrate have been mixed at room temperature with argon ions in energy of 400 keV. Ion beam mixing induced modification of PTCR behavior of the ceramics was studied by using the ac complex impedance method and the resistance vs. temperature measurements. The results showed that room temperature resistance dramatically decreased and Curie point shifted toward higher temperature side for the ion beam mixed samples.