【摘 要】
：
研究了固溶温度对一种新型Al-Cu-Li系合金(2A97铝合金)组织性能的影响。在460～540℃,合金经不同温度固溶处理,水淬后进行相同的时效(165℃×48h)处理。分析了在不同温度固溶处
【机 构】
：
中南大学材料科学与工程学院,中南大学有色金属材料科学与工程教育部重点实验室,
论文部分内容阅读
研究了固溶温度对一种新型Al-Cu-Li系合金(2A97铝合金)组织性能的影响。在460～540℃,合金经不同温度固溶处理,水淬后进行相同的时效(165℃×48h)处理。分析了在不同温度固溶处理的淬火态和时效态合金的显微组织、时效态合金的断口形貌。结果表明:在520℃固溶处理能够使合金充分固溶,时效后有较细小均匀分布的析出相和较多的析出量,时效强化效果最好。
The effect of solution temperature on the microstructure and properties of a new Al-Cu-Li alloy (2A97 aluminum alloy) was studied. At 460-540 ℃, the alloys were treated by solution treatment at different temperatures and subjected to the same aging treatment (165 ℃ × 48h) after water quenching. The microstructures and the fracture morphology of the as-quenched and aged alloys were analyzed at different temperatures. The results show that the solid solution treatment at 520 ℃ can make the alloy fully solution-treated. After aging, there are more fine and uniform precipitates and more precipitates, and the aging strengthening effect is the best.
其他文献
采用单辊甩带法制备了ZK60镁合金薄带,研究了不同条件热处理薄带的组织和显微硬度。结果表明,薄带由晶粒尺寸
孔子曰:“知之者不如好之者,好之者不如乐之者。”教师要较好地培养、爱护学生的学习兴趣,尤其像地理这种内容比较枯燥的学科,更应通过激发学生学习兴趣的方法来提高教学效果
[摘要]百年来，党的理论武装主要经历了制度的形成及曲折发展、重回正轨及制度的恢复发展、制度的深化发展三个阶段，其经验启示包括必须围绕中心服务大局、必须坚持以上率下、必须完善制度建设、必须创新内容和方式方法四个方面。 [关键词]中国共产党;理论武装;历史演进;经验 [中图分类号]D261 [文献标识码]A [文章编号]1009—0274（2021）02—0018—07 [作者简
生态课堂强调尊重学生的个性化发展，凸显每个学生的不同需求和意识，使得教学活动充分建立在学生的差异化学情之上；努力营造出师生之间积极互动的有机生态整体环境，产生教学进程中师生、生生之间的情感共鸣，让学生情知和谐发展，让课堂不仅仅是一个知识传递的场所，寻求课堂内容与形式的变革使之充满生机与活力，促进学生的能动性得以最大化发挥。 1. 多姿现实——让课堂成为一面镜子 激发和保持学生在课堂上的注意力，
党和国家前途命运的根本决定者是创造了历史的人民群众。在我国革命、建设和改革的伟大实践中,中国共产党坚持马克思的人民主体思想,从中国传统文化中的“天下为公”理念和民
2015年10月15日,是习仲勋诞辰102周年纪念日。历史,记录了北京无数条胡同真实的故事和悠长的岁月,也记录了曾居住过那里的历史人物的足迹与身影。后圆恩寺胡同就是典型的代表
新型城镇化是系统的、繁琐的工程,在创建新型城镇化的道路中,我们应该一切从实际入手,坚持以人为中心,坚持马克思主义城乡关系理论,对城镇化的相关规律进行尊重,对人的权益以
团场改革后连队的民主管理取得积极成效,但在具体实施和推进的过程中,连队“两委”和职工群众民主管理的意识与改革发展要求还有一定差距,民主管理的能力和素质有待于提高,民
为确定铝合金脉冲MIG(P-MIG)焊过程稳定性,根据近似熵的理论,对铝合金脉冲MIG焊中的电压信号进行近似熵分析,通过对不同焊接速度、送丝速度与占空比的焊接工艺参数下的电压信