State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Chinese Academy of Sciences,Shenyang, 110015, China)Abstract:The cyclic
Type H defect in 18R martensite in a Cu-Zn-Al alloy has been studied by high resolution electron microscopy. It was found that Type H defect is not fault intern