论文部分内容阅读
It was reported that both dielectricity and magnetism at room temperature were appreciably improved in Bi4Fe2TiO12 film compared with Bi4Fe2TiO12 bulk. X-ray diffraction profiles reveal similar crystalline nature and random orientation of the two, but X-r