A Bi–2.0Zn–0.2Al(wt%) ternary eutectic alloy was prepared using a vacuum melting furnace and a casting furnace. The samples were directionally solidified upwards at a constant growth rate(V = 18.4 μm/s) under different temperature gradients(G = 1.15–3.44