LiFePO4/C composite was synthesized by high temperature solid-state reaction using iron( Ⅱ ) oxalate,ammonium di-hydrogen phosphate and lithium carbonate with
【机 构】
:
School of Metallurgy Science and Engineering
论文部分内容阅读
LiFePO4/C composite was synthesized by high temperature solid-state reaction using iron( Ⅱ ) oxalate,ammonium di-hydrogen phosphate and lithium carbonate with a kind of carbohydrate dissolved in the dispersant(ethanol) as carbon sources added to the synthetic precursor. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy observations(SEM), charge/discharge test, cyclic voltammetry(CV) and carbon analysis. The results show that the synthesis of LiFePO4/C has ordered olivine structure. The carbon has two advantages: optimizing particle size of LiFePO4 and increasing the electronic conductivity and high Li+ diffusivity.The cathode material can demonstrate a charge/discharge flat voltage of 3.4 V(vs Li+/Li). Especially the active material with 15 % and 20% carbohydrate added according to the final product of lithium iron phosphate shows very respectively at 0. 1 C rate and the carbon contents in the final production are only 5.17% and 5.29%, respectively.
其他文献
The non-random two liquids (NRTL) equation together with the Pitzer/Curl Virial equation of state are used to investigate the simultaneous representation of exc
ZnO thin films were deposited on the substrates of (100) γ-LiAlO2 at 400, 550 and 700℃ using pulsed laser deposition (PLD) with the fixed oxygen pressure of 2
The matching performance among the visible and near infrared conting, the low infrared emitting coating and the microwave absorbing coating was investigated. Ex
Photoluminescent(PL) and cathodoluminescent(CL) properties of rare earths (Sc3+, La3+, Gd3+ and Lu3+) doped (Y0.97Tb0.03)2SiO5 were studied. Rare earth doping c
To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the sur
The ternary phase diagrams of musk ketone, musk xylene and various solvent were obtained by calculations. Moreover, the double saturated lines were found to be
通过实地取样、试验及遥感影像分析,分析了河西走廊东部主要地表类型颗粒组成,估算了各地表类型表层土壤潜在尘源总量,分析了潜在尘源与2005年7月17日沙尘暴的关系.研究结果
Self-propagating high-temperature synthesis(SHS) method was used to synthesize ZrB2/Al2O2 composite powders from B2O3-ZrO2-Al system. X-ray diffractometry(XRD)
大气气溶胶污染已成为城市的主要污染问题之一.气溶胶中含有多种毒害污染物,可能对生态或人体健康产生潜在的危害,特别是其可能存在的遗传毒性,已成为政府和人们共同关注的焦
The setting chemistry of glass ionomer cement was investigated by using mechanical determination of compressive strength at predetermined intervals, and measure