Microstructures and mechanical properties of Nb-32Ti-7Al alloys containing different V and Zr contents were investigated. The microstructures were characterized using optical microscopy and scanning electron microscopy (SEM). The alloy with V and Zr presents single phase: Nb solid solution (Nb_(ss)). Tensile testing was carried out at room temperature and 1373 K. The results show that these alloys have good ductility at room temperature. The strengths at room and high temperature increase with the addition of V and Zr, but the room temperature ductility decrease.