在 M P X2000 型盘销式摩擦磨损试验机上,对真空熔烧 Ni基合金 W C复合涂层进行了无润滑的摩擦磨损试验。结果表明,低 W C添加量(25% 、35% )的复合涂层有着优良的耐磨性,而高 W C添加量(60% )涂层的耐磨性则较差。涂层磨损机理主要是磨粒磨损。
In the M P X 2000 type disc wear friction testing machine, the vacuum melting Ni-based alloy W C composite coating was lubricated friction and wear tests. The results show that the composite coating with low W C content (25%, 35%) has excellent wear resistance, while the coating with high W C (60%) shows poor wear resistance. Coating wear mechanism is abrasive wear.