【摘 要】
：
利用Gleeble-1500D热模拟机对Mg-4Al-0.29Mn-0.97Gd镁合金在应变速率为0.1~5.0s-1、变形温度为200~400℃的试验条件下进行热压缩变形行为进行了研究。结果表明,该合金热压缩
论文部分内容阅读
利用Gleeble-1500D热模拟机对Mg-4Al-0.29Mn-0.97Gd镁合金在应变速率为0.1~5.0s-1、变形温度为200~400℃的试验条件下进行热压缩变形行为进行了研究。结果表明,该合金热压缩时发生了动态再结晶;试样边缘部分的变形机制主要为孪晶,而试样中部的变形机制主要为再结晶;变形温度和应变速率综合影响镁合金的热压缩变形过程。
The hot compressive deformation behavior of Mg-4Al-0.29Mn-0.97Gd magnesium alloy under the experimental conditions of strain rate of 0.1 ~ 5.0s-1 and deformation temperature of 200 ~ 400 ℃ was studied by Gleeble-1500D thermal simulator. The results show that the dynamic recrystallization occurs during the hot compression of the alloy. The deformation mechanism of the edge of the sample is mainly twins, while the deformation mechanism of the middle part of the sample is mainly recrystallization. The deformation temperature and strain rate affect the thermal compression of the magnesium alloy Deformation process.
其他文献
采用扫描电镜、X射线衍射仪等分析手段,研究了热处理工艺对离心铸造变质无限冷硬铸铁轧辊组织和性能的影响。结果表明,变质无限冷硬铸铁轧辊的铸态组织是贝氏体+碳化物+少量
高阻尼合金构件工作时易于操控,减少噪声,ZA合金具有高的阻尼性能,作为阻尼材料具有很好的发展前景。综述了ZA合金阻尼特性的研究进展,介绍了ZA合金的组织特点和阻尼特性的机
以TiB2/Cu复合粉末压坯为研究对象,应用微波烧结炉对其进行烧结。探讨了微波烧结制备TiB2/Cu复合材料的几种基本的工艺因素。结果表明,在微波烧结条件下,以SiC粉末作为辅助加
利用液相烧结法制备了一种Al-10SiC/Al4C3中间合金,并将其用于细化AZ63合金。X射线衍射分析结果表明,Al-10SiC/Al4C3中间合金的相组成除α-Al外,主要为Al4C3相、Si相以及未反
围生期死亡率是衡量一个地区医疗卫生和妇幼保健工作质量的一项重要指标[1,2],而在围生儿死亡构成比中,胎儿宫内死亡占大多数[3].为进一步做好妇幼保健工作,降低围生期死亡率,我们对19 423例分娩的孕产妇进行调查,现将结果报告如下。
慢性前列腺炎(chronic prostatitis,CP)是泌尿外科门诊最常见的疾病之一,慢性盆腔疼痛综合征(Chronic pelvic pain symptoms,CPPS)属于美国国立卫生研究院(NIH)前列腺炎分类系统中的Ⅲ型,是CP中最常见的类型,由于其临床表现不一,治疗效果不佳,且易复发,因此临床上常有过度治疗的现象,如何恰当治疗一直是困扰泌尿外科医生的一个问题.笔者回顾分析163例
Dieulafoy病是上消化道大出血的少见病因,出血量大且反复发作,出血部位隐匿,极易误诊漏诊,病死率高.近年来,随着内镜诊疗技术广泛开展,确诊率得以提高,病死率逐年下降.我院近十年共收治本病13例,现报告如下。
大型筒体铸件采用ZL101A铝合金材料铸造,简体总长1 410 mm,直径为φ615 mm,质量为223 kg,铸件表面不能有夹渣、针孔、缩孔、缩松等缺陷,并且需要承受FS6气密性检验.该简体铸
介绍了防止薄壁铸件消失模模样变形的工艺措施,分析了消失模模样制作的工艺流程与控制重点。射粒时,进料口应放置在进料阻力最小的位置;薄壁大平面处应少布置气塞,厚壁处多设
手术切除是治疗肝门部胆管癌的主要手段,因其特殊的解剖关系及肿瘤特性,所以根治切除率低,治疗效果不理想[1].我院2005年至2006年共收治26例肝门部胆管癌患者,其中14例行根治切除,取得较好疗效.现报告如下。