The partial and the integral enthalpies of mixing of liquid Al-Cr and Ni-Cr binary alloys have been determined by high temperature isoperibolic calorimetry at 1723±5 K and 1729±5 K, respectively. The results were analytically described by the thermodynamically adapted power series (TAPS). The enthalpies of mixing values for both binary liquid melts are small and negative and in good agreement with the available literature data. Minima of the mixing enthalpies of liquid Al-Cr and Ni-Cr alloys are -7.0 kJ·mol-1 at 46 at. pct Cr and -3.0 kJ·mol-1 at 37 at. pct Cr, respectively.
The partial and the integral enthalpies of mixing of liquid Al-Cr and Ni-Cr binary alloys have been determined by high temperature is pertribolic calorimetry at 1723 ± 5 K and 1729 ± 5 K, respectively. The results were analytically described by the thermodynamically adapted power series (TAPS). The enthalpies of mixing values for both binary liquid melts are small and negative and in good agreement with the available literature data. Minima of the mixing enthalpies of liquid Al-Cr and Ni-Cr alloys are -7.0 kJ · mol -1 at 46 at. Pct Cr and -3.0 kJ · mol-1 at 37 at. Pct Cr, respectively.