论文部分内容阅读
利用不同的热处理制度对NiAlMn高温形状记忆合金进行有序化处理,并通过室温X射线衍射分析,得到NiAlMn合金的马氏体结构为3R。有序度的大小可以利用特征线对的面间距Δd来表示。结果表明,分级淬比上淬更有利于合金的有序化
The NiAlMn high temperature shape memory alloy was ordered by different heat treatment systems, and the martensite structure of the NiAlMn alloy was 3R by room temperature X-ray diffraction analysis. The degree of ordering can be expressed by the interplanar spacing Δd of the characteristic line pairs. The results show that the grade quenching quenching more conducive to the ordering of the alloy