The composite nanofibers of SrTiO3/SrFe12O19 with a molar ratio of 1:1 and diameter about 120 nm were prepared by electrospinning. Effects of calcination temperature on the formation, crystallite size, morphology and magnetic property were studied by infrared spectroscopy, X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer. The binary phase of strontium ferrite and titanate was formed after being calcined at 900℃ for 2 h and the composite nanofibers were fabricated from nanograins of SrTiO3 about 24 nm and SrFe12O19 around 33 nm. The crystallite sizes for the nanofibers increase with increasing calcination temperature and the addition of SrTiO3 has an obvious suppression effect on SrFe12O19 grain growth. The specific saturation magnetization and remanence tend to increase with the crystallite size. With increasing calcination temperature from 900 to 1050℃, the coercivity increases initially, achieving a maximum value of 520.2 kA·m-1 at 950℃, and then shows a reduction tendency.
The composite nanofibers of SrTiO3 / SrFe12O19 with a molar ratio of 1: 1 and diameters about 120 nm were prepared by electrospinning. Effects of calcination temperature on the formation, crystallite size, morphology and magnetic properties were studied by infrared spectroscopy, X-ray diffraction , scanning electron microscopy and vibrating sample magnetometer. The binary phase of strontium ferrite and titanate was formed after 900 ° C for 2 h and the composite nanofibers were fabricated from nanograins of SrTiO3 about 24 nm and SrFe12O19 around 33 nm. The crystallite sizes for the nanofibers increase with increasing calcination temperature and the addition of SrTiO3 has an obvious suppression effect on SrFe12O19 grain growth. With specific calcification temperature from 900 to 1050 ° C, the coercivity increases initially, achieving a maximum value of 520.2 kA · m-1 at 950 ° C, and th en shows a reduction tendency.