Fabrication and Thermal Properties of a New Heat Storage Concrete Material
【机 构】
:
School of Materials Science and Engineering,Wuhan University of Technology,Wuhan 430070,China;The Ce
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2010年4期
其他文献
Preparation and Characterization of V-K Catalysts Supported on Porous α-alumina Ceramic Substrate fo
The V-K catalysts were produced on porousα-alumina substrate by a solution im-pregnation route and the compositions and catalytic activities for soot oxidation were studied by XRD, TG/DTG,DSC and TPR.According to the catalytic activity studies,the catalyt
Utilizing pre-cast ECC panels as participating permanent formwork of concrete members,and the validity of using ECC to disperse the single crack in concrete into multiple ones in ECC were studied.In the process,totally two kinds of ECC with different tens
The Enhancement of Osteogenesis by Scaffold Based on Mineralized Recombinant Human-like Collagen Loa
A biomimetic scaffold based on mineralized recombinant collagen,nano-hydroxyapatite/recombinant human-like collagen/poly(lactic acid)(nHA/RHLC/PLA),was prepared with recombinant human bone morphogenic protein-2(rhBMP-2)for improving the os-teoinductive pr
Numerical Analysis of Fiber Bragg Grating and Long Period Fiber Grating Undergoing Linear and Quadra
The coupled-mode equations for fiber Bragg grating(FBG)and long period fiber grating(LPFG)undergoing linear and quadratic temperature change were given.The effects of tem-perature gradient and quadratic temperature change on the reflectivity spectrum of f
The pozzolanic reactivity was determined by the hydration kinetics of pozzolanic reaction based on the fact that the hydration products of active SiO_2 and Al_2O_3 with lime were soluble in dilute hydrochloric acid.The results show that the pozzolanic rea
A series of new polyamides 3a-d containing aryl-azo,ether and sulfone groups in the main chain were synthesized from bis[4-(4-aminophenoxy)phenyl sulfone]1 and several azo aromatic diacyl chlorides 2a-d by the low temperature solution polycondensation tec
Doping of boron,nitrogen,aluminum and titanium in the SiC(310)twin boundary was investigated,and the first-principle calculation was used to analyze the underlying mechanism of excellent creep resistance and strength of Sylramic and Tyranno SA SiC fibers.