According to the analysis of the macro and micro characteristics of the center of continuous casting blooms by acid wash, SEM, metallographic and scanning-type electron microscope, there was a serious segregation and some shrinkage cavities in the slab; Cracks occurred at the end of the columnar crystal and spread along the boundary of the primary dendrite. At the crack enriched a large number of impurity elements, carbon, phosphorus, sulfur, whose crystal boundary segregation is the internal factor of the intermediate cracks. Determining the originated location of intermediate cracks and calculating the total strain in this area during solidification process of slab, it is found that the load is the ex- ternal factor of cracks’ generation and expansion.
According to the analysis of the macro and micro characteristics of the center of continuous casting blooms by acid wash, SEM, metallographic and scanning-type electron microscope, there was a serious segregation and some shrinkage cavities in the slab; Cracks occurred at the end of the columnar crystal and spread along the boundary of the primary dendrite. At the crack enriched a large number of impurity elements, carbon, phosphorus, sulfur, whose crystal boundary segregation is the internal factor of the intermediate cracks. Determining the originated location of intermediate cracks and calculating the total strain in this area during solidification process of slab, it is found that the load is the ex-ternal factor of cracks’ generation and expansion.