分析了三相分离器失效的原因，认为造成该分离器失效的主要原因为沟状腐蚀。阐述了沟状腐蚀发生的原因及过程，最后提出了防止该类分离器失效的措施及方法。
The reason of the failure of the three-phase separator was analyzed. It is considered that the main reason of the failure of the separator is the groove corrosion. The reason and process of groove corrosion are expounded. Finally, measures and methods to prevent the failure of such separator are put forward.