Two types of small iron clusters supported onγ-Al2O3-RT(dehydroxylated at room temperature) andγ-Al2O3-800 (dehydroxylated at 800℃) were prepared by solvated metal atom impregnation (SMAI) techniques. The iron atom precursor complex, bis(toluene)iron(0) formed in the metal atom reactor, was impregnated intoγ-Al2O3 having different concentrations of surface hydroxyl groups to study the effect of surface hydroxylation on the crucial stage of iron cluster formation. Catalysts prepared in this way were characterized by TEM, Mossbauer, and chemisorption measurements, and the results show that higher concentration of surface hydroxyl groups ofγ-Al2O3-RT favors the formation of more positively charged supported iron cluster Fen/γ-Al2O3-RT, and the lower concentration of surface hydroxyl groups ofγ-Al2O3-800 favors the formation of basically neutral supported iron cluster Fen/γ-Al2O3-800. The measured results also indicate that the higher concentration of surface hydroxyl groups causes the rapid decomposition of precursor complex, bis(toluene)iron(0), and favors the formation of relatively large iron cluster. Consequently, these two types of catalysts show different catalytic properties in Fischer-Tropsch reaction. The catalytic pattern of Fen/γ-Al2O3-RT in F-T reaction is similar to that of the unreducedα-Fe2O3 and that of Fen/γ-Al2O3-800 is similar to that of the reducedα-Fe2O3.
Two types of small iron clusters supported on γ-Al2O3-RT (dehydroxylated at room temperature) and γ-Al2O3-800 (dehydroxylated at 800 ° C) were prepared by solvated metal atom impregnation (SMAI) techniques. The iron atom precursor complex, bis ) iron (0) formed in the metal atom reactor, was impregnated into γ-Al2O3 having different concentrations of surface hydroxyl groups to study the effect of surface hydroxylation on the crucial stage of iron cluster formation. Catalysts prepared in this way were characterized by TEM, Mossbauer, and chemisorption measurements, and the results show that higher concentration of surface hydroxyl groups of γ-Al2O3-RT favors the formation of more positively charged supported iron cluster Fen / γ-Al2O3-RT, and the lower concentration of surface hydroxyl groups of γ- Al2O3-800 favors the formation of substantially neutral supported iron cluster Fen / γ-Al2O3-800. The measured results also indicate that higher concentration of surface hydroxyl groups cause The rapid decomposition of precursor complex, bis (toluene) iron (0), and favors the formation of relatively large iron cluster. These two types of catalysts show different catalytic properties in Fischer-Tropsch reaction. The catalytic pattern of Fen / γ-Al2O3-RT in FT reaction similar to that of the unreduced α-Fe2O3 and that of Fen / γ-Al2O3-800 is similar to that of the reduced α-Fe2O3.