The (Ti0.85Zr0.15)1.05Mn1.2Cr0.6V0.1M0.1 (M=Ni, Fe, Cu) alloys with a single C14-type Laves phase have been fabricated by arc melting. They are able to be easil
Fine NP-AgAu (nanoporous AgAu) alloys with spongy structure was fabricated by chemical dealloying from rapidly solidified amorphous precursors Ag38.75?xCu38.75S