The full densification polycrystalline cerium hexaboride (CeB6) cathode material was prepared by using the spark plasma sintering (SPS) method in an oxygen free
【机 构】
：
Key Laboratory of Advanced Functional Materials. Ministry of Education
论文部分内容阅读
The full densification polycrystalline cerium hexaboride (CeB6) cathode material was prepared by using the spark plasma sintering (SPS) method in an oxygen free system. The starting precursor nanopowders with an average grain size of 50 nm were prepared by high-energy ball milling. The ball-milled nanopowder was fully densified at 1550 ℃ under 50 MPa, which was about 350 ℃ lower than the conventional hot-pressing method and it was also lower than that of coarse powder under the same sintering condition. The mechanical properties of nanopowder sintered samples were significantly better than that of coarse powder, e.g., the flexural strength and Vickers hardness were 211% and 51% higher than that of coarse powder, respectively. The electron backscattered diffraction (EBSD) result showed that the (100) fiber texture could be fabricated by the ball-milled nanopowder sintered at 1550 ℃ and the thermionic emission current density was measured to be 16.04 A/cm2 at a cathode temperature of 1873 K.
其他文献
Al合金表层的缺陷常常会导致腐蚀发生.因此,采取保护措施以提高铝合金的抗腐蚀性能是非常重要的.从电化学的角度出发,对固溶、淬火和时效处理工艺进行优化,以提高铝合金的强
钛合金由于具有高比强度、优越的耐腐蚀性和出色的耐热性等优良特性,已成功应用于航空航天、造船和化学工业.尽管钛合金具有合适的可焊性特点,但焊接方法极大地影响焊接接头
The mutual destabilization between complex hydrides and lithium amide has been comprehensively reported. In this paper, CeH2 doped Li-Mg-N-H/NaA1H4 composite wa
The effects of Ce, Y and Gd additions on the as-cast microstructure and mechanical properties of Mg-3Sn-lMn alloy were investigated and compared by using optica
轻型纸是一种纸质疏松、表面平滑、印刷性能好的印刷用纸。采用西康80/48阔叶木化机浆替化针叶木化机浆生产轻型纸,产品具有强度好,平滑度高,成本下降等特点。纸的松厚度,经
酶在制浆造纸工业中的应用,从20世纪80年代中期起迅速发展起来。化学浆的磨浆或打浆是生产纸及纸板极为关键的工段。分析了打浆酶预处理对漂白针叶木浆(NBKP)和漂白阔叶木浆(
The structure and high-temperature electrochemical properties of the as-cast and annealed (940 ℃, 8 h) La0.60Nd0.15Mg0.25Ni3.3Si0.10 hydrogen storage alloys we
We reported on the successful synthesis of the Nd:YAG (Nd:Y3Al5O12) nano-powders by using urea as the precipitant with the microwave assisted homogeneous precip
纸张通常有定量稳定,厚薄适中,布浆均匀,内在、外观质量良好的要求。介绍了采用纸张的定量、厚度、均匀度的自动监控技术,实施生产、技术管理,对确保产品质量,提高生产效率,
The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Eu(NO3)3·6H2O under the hydrothermal conditions gave a 3D coordination polymer, Eu2(BIPA)3(CH3CH2OH)