【摘 要】
：
The reinforcement/matrix interfacial strength has been considered as the key factor when glass ifber reinforced polymer (GFRP) bar is mixed with concrete. In this paper, based on micromechanics, four-point bending numerical models with and without glass i
【机 构】
：
Faculty of Civil Engineering, Guangzhou University, Guangzhou 510006, China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The reinforcement/matrix interfacial strength has been considered as the key factor when glass ifber reinforced polymer (GFRP) bar is mixed with concrete. In this paper, based on micromechanics, four-point bending numerical models with and without glass ifber of different interfacial strength have been set up to simulate the damage process of GFRP reinforced concrete beam. The results show that the higher the interfacial strength is, the higher the ultimate bearing capacity of beams, and the less the opening width and height of cracks will be reached. Furthermore, mixing of glass ifbers has less inlfuence on the damage process when the interfacial strength is weak, however, it can help to improve the ultimate bearing capacity of the beams, retard the expansion of cracks and improve the toughness when the interfacial strength is high.
其他文献
In order to evaluate the feasibility of using phase change materials to reduce the inner temperature rise of mass concrete, the interior temperature of normal concrete specimen under semi-adiabatic curing condition was measured. The effect of embedding ph
A series of polycarboxylate-based superplasticizers (PCs) with different structures were synthesized and the effects of chemical structure on zeta potential and rheological property of cement paste were studied. Residual monomers in each sample of PCs wer
P(BA-GMA) (PBG), having various molecular weights, was synthesized by in situ polymerization of butyl acrylate (BA) and glycidyl methacrylate (GMA), and further used as a modifier to improve the comprehensive properties of the epoxy curing system. The cop
High-temperature thermal storage material is one of the critical materials of solar thermal power generation system. Andalusite, kaolin, talc,γ-Al2O3 and partially stabilized zirconia were used as the raw materials, and in-situ synthesis of cordierite was