本文研究了3%硅钢所析出的AlN和MnS的完全固溶温度,并测定了其固溶度乘积:log{[Al%][N%]}=-10062/T+2.72;10g{[Mn%][S%]}=-14855/T+6.82还得出了AlN和MnS的连续冷却析出曲线。
In this paper, the complete solution temperature of AlN and MnS precipitated in 3% silicon steel was studied and the product of its solid solubility was determined: log {[Al%] [N%]} = - 10062 / T + 2.72; %] [S%]} = -14855 / T + 6.82 A continuous cooling precipitation profile for AlN and MnS was also obtained.