【摘 要】
：
The adsorption amount of poly(styrene sulfonate) and poly(dimethyldiallyl ammonium chloride) (PSS/PDDA) self-assembled multilayer membranes in designed dipping
【机 构】
：
Department of Polymer Science & Engineering,Department of Chemical and Materials Engineering
论文部分内容阅读
The adsorption amount of poly(styrene sulfonate) and poly(dimethyldiallyl ammonium chloride) (PSS/PDDA) self-assembled multilayer membranes in designed dipping solvents were measured by UV-Vis-spectroscopy and quartz crystal microhalance (QCM). Intrinsic viscosities of PSS and PDDA in corresponding dipping solvents were determined by an Ubbelohde viscometer. It is found that the adsorption amount of PSS/PDDA self-assembled multilayer membranes built up in different dipping solutions, added salt concentration, pH of solution and solvent quality, respectively changed oppositely with the corresponding intrinsic viscosity of PSS and PDDA in dipping solvents. A negative relation between the adsorption amount and intrinsic viscosity was revealed, and explained in term of the concept of excluded volume of polymer molecule in dilute solutions.
其他文献
Warm compaction and room temperature compaction were applied to prepare bonded Nd-Fe-B magnets. The results indicated that the density of magnet was determined
Carbon materials were prepared using mesoporous silica HMS with different pore sizes as the hard templates and water-soluble phenolic resin as the carbon source
The settling and hydrodynamic properties of 3-D fractal flocs in quiescent water are investigated with a numerical model based on the Lattice Boltzmann Method (
Thermosetting acrylic coatings were prepared by using carboxyl acid group-containing acrylic oligomer and curing with titanium-oxo-clusters which were first pre
Ammonium metavanadate(10 mol%) was found to be a useful catalyst for the synthesis of various 2-substituted aryl benzimidazoles.It was used as an oxidizing agen
This paper considers the problem of planning the motion of a searcher in a polygonal region to eventually "see" an intruder that is unpredictable and capable of
Novel Cu-Ni/C has been prepared and utilized as an efficient catalyst system in direct synthesis of DMC from CH3OH and CO2.
FeO_x-SiO_2 catalysts prepared by a sol-gel method were studied for the selective oxidation of methane by oxygen. A single-pass formaldehyde yield of 2.0% was o
Mesoporous silica supported CS2.5Ho.sPWI2040 catalysts were prepared by impregnation method, and several silica supports with different pore size were utilized.
Multiple performance requirements need to be guaranteed in some real-time applications such as multimedia data processing and real-time signal processing in add