Synthesis of Ni0.5LixZn(0.5-x)Fe2O4 nanoparticles with x=0, 0.1, 0.2, 0.3, 0.4 and 0.5 were realized via co-precipitation method. X-ray diffraction (XRD) and vibrating sample magnetometer (VSM) measurements were performed on the samples to determine the characteristics of the crystal structures and the magnetic properties of the samples, respectively. The spinel phase structures of the samples were confirmed by XRD analysis. Patterns of decreased lattice parameter and increased crystallite size values were observed by increasing the Li concentration at longer synthesis reaction periods. Similarly, for the magnetic properties, both the saturation magnetization (Ms) and coercivity (Hc) were found to vary with increasing patterns at higher Li doping levels and longer synthesis reaction periods. The results and mechanisms concerned were discussed.
Synthesis of Ni0.5LixZn (0.5-x) Fe2O4 nanoparticles with x = 0, 0.1, 0.2, 0.3, 0.4 and 0.5 were realized via co-precipitation method. X-ray diffraction (XRD) and vibrating sample magnetometer performed on the samples to determine the characteristics of the crystal structures and the magnetic properties of the samples, respectively. The spinel phase structures of the samples were confirmed by XRD analysis. Patterns of decreased lattice parameter and increased crystallite size values were observed by increasing the Both the saturation magnetization (Ms) and coercivity (Hc) were found to vary with increasing patterns at higher Li doping levels and longer synthesis reaction periods. The results and mechanisms concerned were discussed.