【摘 要】
：
The properties and structure of electrodeposited RE (CeO2)-Ni-W-P-SiC composite coating were investigated. The results show that the hardness and electrodeposit
【机 构】
：
College of Materials Science and Engineering
论文部分内容阅读
The properties and structure of electrodeposited RE (CeO2)-Ni-W-P-SiC composite coating were investigated. The results show that the hardness and electrodepositing speed of composite coatings obtained at an impulse current are higher than those at a direct current. The hardness and wear resistance of the coating are obviously increased by adding RE and SiC. The hardness of the coating increases with the increase of treatment temperature and current density, and reaches the optimum value at 400 ℃ and at 10 A/dm2, respectively. The optimum operation parameters of electrodeposition of the composite coating are as follows: pH value is 4.5, bath temperature is 65 ℃, and current density is 10 A/dm2.
其他文献
Four types of steel sheets containing 0.04%, 0.09%, 0.14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 μm in thickness and then g
Stable binary single source precursors (SSP) for the deposition of thin films of ceramic semiconductors of composition SnO·GeO were synthesized by close circui
The amorphous Fe78Si9B13 ribbons were bend stress relaxed at various temperature well below the crystallization temperature (Tx) for different time. The effect
Using spark plasma sintering(SPS) technique, TiC particle reinforced γ-TiAl composites were prepared with varying weight fraction of TiC powders. The effects o
Spherical icosahedral quasicrystalline phase (I-phase) was obtained by introducing Ca into Mg-Zn-Y alloy under conventional casting conditions. Due to the addit
研究了非正定方差阵下,证券组合投资模型的最优投资比例系数的计算,有效边界,冗余证券的数量以及套利机会.从而为实证分析提供了理论依据和方法.
This paper studies the ca
A novel carbon-sulfur nano-composite material was synthesized by heating sublimed sulfur and high surface area activated carbon (HSAAC) under certain conditions
The effects of two-stage aging and retrogression and reaging heat treatment on the fracture toughness and stress corrosion cracking resistance of 7475 alloy wer
The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems o
走出国门获取资源类产品是保障国民经济发展的重要手段.浙江民营企业在"走出去"的实践中取得了相当的成绩,但也还存在不少问题.本文分析了"走出去"的多种形式,建议企业要充分