【摘 要】
:
Reaction-bonded B4C–SiC composites are highly promising materials for numerous advanced technological applications. However, their microstructure evolution mechanism remains unclear. Herein, B4C–SiC composites were fabricated through the Si-melt infiltrat
【机 构】
:
State Key Laboratory of Materials Processing and Die&Mould Technology,School of Material Science and
论文部分内容阅读
Reaction-bonded B4C–SiC composites are highly promising materials for numerous advanced technological applications. However, their microstructure evolution mechanism remains unclear. Herein, B4C–SiC composites were fabricated through the Si-melt infiltration pro-cess. The influences of the sintering time and the B4C content on the mechanical properties, microstructure, and phase evolution were investig-ated. X-ray diffraction results showed the presence of SiC, boron silicon, boron silicon carbide, and boron carbide. Scanning electron micro-scopy results showed that with the increase in the boron carbide content, the Si content decreased and the unreacted B4C amount increased when the sintering temperature reached 1650℃ and the sintering time reached 1 h. The unreacted B4C diminished with increasing sintering time and temperature when B4C content was lower than 35wt%. Further microstructure analysis showed a transition area between B4C and Si, with the C content marginally higher than in the Si area. This indicates that after the silicon infiltration, the diffusion mechanism was the primary sintering mechanism of the composites. As the diffusion process progressed, the hardness increased. The maximum values of the Vickers hardness, flexural strength, and fracture toughness of the reaction-bonded B4C–SiC ceramic composite with 12wt% B4C content sintered at 1600℃ for 0.5 h were about HV 2400, 330 MPa, and 5.2 MPa·m0.5, respectively.
其他文献
The silicon-based material exhibits a high theoretical specific capacity and is one of the best anode for the next generation of advanced lithium-ion batteries (LIBs). However, it is difficult for the silicon-based anode to form a stable solid-state inter
水利项目造福于国家和人民,为了改善民生和人们的生活质量,水利项目的建设目前正在迅速发展.但是,水利项目与其他工程的不同之处在于,工程范围广泛、重点多、难度大.不良的施工质量不可避免地导致各种事故的频繁发生,会产生工程事故隐患,让人民生命财产受到损失.多年的水利项目事故案例让人们痛心疾首,我们需要加强对建设项目质量的监控,以确保水利项目的高质量和高品质.
艺术设计离不开立体构成,立体构成也是艺术设计审美中最重要的组成部分.立体构成主要着重于构造空间立体模型,换言之,立体构成就是将某种造型展示在三维空间中,形成一种立体感和在固定空间中的形态,而环境设计则是指利用立体构成技术的方式,将某建筑的内外环境空间二次建造的过程,并通过该技术将实际物质进行空间构造.
环保约谈是中央生态环保督察工作中重要环节之一,能够有效缓解经济发展与环境保护之间的关系.环保约谈作为一种软约束力,能够有效监督地方政府提高环保意识,规范企业排污规范化,但依旧存在着相关法律制度不完善、监管部门不到位、公众环保意识薄弱等问题.在我国大力推动生态环保督察的背景下,对环保约谈这种监督方式进行探讨并提出完善建议.
“城中村”是我国社会发展中一种不可回避的社会现象,是城乡二元化在城镇化进程中的产物.由于“城中村”建设先天缺少消防规划,建筑密度过大,居住人员缺乏消防安全意识,已成为火灾事故频发的重灾区.
Hot compression tests were performed on AISI 321 austenitic stainless steel in the deformation temperature range of 800–1200°C and constant strain rates of 0.001, 0.01, 0.1, and 1 s−1. Hot flow curves were used to determine the strain hardening exponent a
Cobalt (Co)-modified brownmillerite KBiFe2O5 (KBFO; [KBiFe2(1−x)Co2xO5 (x = 0, 0.05)]) polycrystalline is synthesized following the solid-state reaction route. Rietveld refinement of X-ray diffraction data confirmed the phase purity of KBFO and KBiFe1.9Co
随着现代社会的发展,电视新闻工作者的工作内容不仅是为广播站服务,还需要在一些媒体上面进行一些新闻的发布以及一些其他的工作,但是按照以前的工作模式很难完成这样的工作,因此媒体融合的重要性就显现出来了.
The microstructural properties and electrochemical performance of zinc (Zn) sacrificial anodes during strain-induced melt activation (SIMA) were investigated in this study. The samples were subjected to a compressive ratio of 20%–50% at various temperatur
MnO2/biomass carbon nanocomposite was synthesized by a facile hydrothermal reaction. Silkworm excrement acted as a carbon precursor, which was activated by ZnCl2 and FeCl3 combining chemical agents under Ar atmosphere. Thin and flower-like MnO2 nanowires