Aluminum borate whiskers (9Al 2O 3·2B 2O 3) can be used to reinforce aluminum alloys to produce light and strong composites. However, the adverse interfacial reactions between the whiskers and the aluminum alloys inhibit their practical uses; therefore, a protective coating is needed on whiskers. In this work, aluminum borate whiskers were coated with chromium coating deposits in a hydrothermal solution containing CrCl 3, Na 2C 4H 4O 6, NaPH 2O 2, and H 3BO 3. The presence of the impurity P in the hydrothermal deposits can be avoided by reducing the amount of NaPH 2O 2 in the coating solution. Thermodynamic analysis was used to discuss the behavior of ions in the coating process. The subsequent heating of the hydrothermal products in air at 800 ℃ yielded smooth Cr 2O 3 films with a thickness of 0.060.07 μm.
However, the adverse interfacial reactions between the whiskers and the aluminum alloys inhibit their practical uses; therefore, a protective coating is needed on whiskers. In this work, aluminum borate whiskers were coated with chromium coating deposits in a hydrothermal solution containing CrCl 3, Na 2C 4H 4O 6, NaPH 2O 2, and H 3 BO 3. The presence of the impurity P in the hydrothermal deposits Thermodynamic analysis was used to discuss the behavior of ions in the coating process. The subsequent heating of the hydrothermal products in air at 800 ° C yielded smooth Cr 2O 3 films with a thickness of 0.060.07 μm.