【摘 要】
：
By using the spark plasma sintering process, Ti2AlC/TiAl composite with the addition of Niobium (Nb) was prepared in-situ and the microstructure of Ti2AlC/TiAl
【机 构】
：
Shod of Materials Science and Technology,State Key Laboratory of Advanced Technology for Materials S
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
By using the spark plasma sintering process, Ti2AlC/TiAl composite with the addition of Niobium (Nb) was prepared in-situ and the microstructure of Ti2AlC/TiAl (Nb) composite was investigated by means of transmission electron microscopy (TEM) and high-resolution electron microscopy (HREM).The results indicate that new-formed Ti2AlC particles disperse with a high degree of uniformity and well combine with the matrix. In the area of phase interface the d-spaces of Ti2AlC (100) and TiAl (110) were measured as 0.2648 nm and 0.2991 nm,respectively. The atom arrangement beside the interface was only partly corresponding, existing in semicoherent state. On the contrary, in the area of grain interface the d-spaces of TiAl(100) and TiAl (110) were measured as 0.2462 nm and 0.2631 nm,respectively and the atom arrangement beside the interface was almost corresponding, existing in coherent state.
其他文献
Alumina nanostructures were obtained by two-step anodization process. The porous anodic aluminum oxide(AAO) membranes were anodized in oxalic acid, which was su
The effect of cooling rate after 40% hot deformation on structure and mechanical properties of low alloy wear resistance cast iron was investigated by metallogr
The effects of an external DC (direct current) electric field on recrystallization texture evolution in the cold-rolled aluminum sheets with 99.99% purity were
幼羔胚胎体外生产技术（JIVET）是全球草食类动物繁殖技术中最先进的生物工程技术。国内外对幼羔经激素诱导后生产胚胎已作了许多研究,并取得一定的成果,本文就其研究进展作一综
Effects of milling and crystallization conditions on microstructure, such as amorphous phase and nanocrystalline phase, were investigated by X-ray diffractometr
A novel novolac curing agent containing both naphthalene and dicyclopentadiene (DCPD) moieties was prepared to produce a highly heat-resistant cured polymer net
The corrosion behavior of Cu-Cr alloy in 3.5% NaCl + NH3 solution had been studied, and the influences of the concentration of NH3 on corrosion resistance discu
Uniform crystalline TiO2 thin films were coated on silica glass fibers by liquid phase deposition from aqueous solution of ammonium hexafluorotitanate at low te
The effects of different substrates on the structure and hydrogen evolution from a-Si:H thin films deposited by plasma enhanced chemical vapour deposition were
A series of nanocomposite thin films, composed of Nd2Fe14B and α-Fe, has been prepared by DC-magnetron sputtering combined ion beam sputtering onto Si (100) su