Effect of Intercritical Annealing Time on the Microstructures and Tensile Properties of a High Stren

来源 :Acta Metallurgica Sinica(English Letters) | 被引量 : 0次 | 上传用户:rmbsaxn
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
A new Mn–Si–Al–Mo–Nb transformation-induced plasticity steel was annealed by intercritical annealing for different durations to investigate the partitioning of C element and the volume fraction change of the microstructural constituents. Direct experimental evidence confirms the partitioning of C elements in different phases during heat treatment by Electron probe microanalysis and X ray diffraction. The distribution of the precipitates was investigated as well. It was revealed that the microstructures and mechanical properties of the investigated steels were affected by the intercritical annealing time. According to the present experiment, the volume fraction of retained austenite and the product of tensile strength and total elongation of investigated steel decrease with increasing intercritical annealing time. It was observed that high tensile strength of 1,103 MPa, total elongation of 21.3%, and strength-ductility product of 23,493.9 MPa % could be successfully produced in this experimental steel at intercritical annealing temperature of 830 °C, holding for 1 min, and isothermal bainite treatment of 440 °C for 5 min holding time. A new Mn-Si-Al-Mo-Nb transformation-induced plasticity steel was annealed by intercritical annealing for different durations to investigate the partitioning of C element and the volume fraction change of the microstructural constituents. Direct experimental evidence confirms the partitioning of C elements in different phases during heat treatment by Electron probe microanalysis and X ray diffraction. It was revealed that the microstructures and mechanical properties of the investigated steels were affected by the intercritical annealing time. According to the present experiment, the volume fraction of retained austenite and the product of tensile strength and total elongation of investigated steel decrease with increasing intercritical annealing time. It was observed that high tensile strength of 1,103 MPa, total elongation of 21.3%, and strength-ductility product of 23,493.9 MPa% could be successfully produced in this experimental steel at intercritical annealing temperature of 830 ° C, holding for 1 min, and isothermal bainite treatment of 440 ° C for 5 min holding time.
其他文献
通过在Co_(82)Zr_(18)合金中添加过渡族元素Cr的方法,利用快淬工艺,制备出了Co_(82-x)Zr_(18)Cr_x(x=0,2,3,4)快淬合金薄带,利用磁性测量、X光衍射、热磁分析、扫描电子显微
2015年11月27日,王思聪旗下的“香蕉计划”获得LPL2016承办权。  据透露,央视著名体育解说段暄成为香蕉计划体育CEO。此外,香蕉计划会邀请韩国OGN直播团队来负责LPL赛事。过去十年,我们一直在感叹韩国电竞赛事的专业。王思聪大手一挥,师夷长技以制夷,韩国人的到来,不仅能打造更为专业的LPL赛事转播,还可以培养熏陶国内电竞转播团队。  实际上,所谓的香蕉计划,只是2015年王校长电竞组合
足球运动是现阶段一种普遍的大众运动,也是我国高校体育教学中的重要组成部分,在高校体育教学中有着极其中重要的地位。本文主要阐述了在高校体育足球教学中应用足球游戏教学
健身气功是在祖国传统中医养生理论的指导下,通过特定的肢体运动,同时配合呼吸以及意念来调节人体身心健康的一种身心锻炼方法。随着几种普及功法的推广,越来越多的群众参与
为了满足安全壳过滤排放系统的气溶胶过滤性能测试实验的要求,进行实验用气溶胶选取的方案研究。对安全壳内气溶胶实际特性进行计算评估,得出严重事故后安全壳内气溶胶的特性
西门子工业业务领域冶金技术部获得来自中国钢铁企业青岛特殊钢铁有限责任公司(青钢)的合同,为青钢提供一套扁钢轧机。这套新轧机的年产能力为60万t,生产的扁钢宽度为60~160m
道教是中国土生土长的宗教,产生于东汉顺、桓之际,以五斗米道和太平道的呈现为基本标记。在漫长的历史成长中,道教还传到朝鲜、日本、越南及东南亚一带,甚至还远渡重洋,传到
采用文献资料法,问卷调查法,实地调查法,抽样调查法对内江市各地区的社区体育现状进行调查研究。研究结果表明,内江市绝大多数地区,社区体育建设相对落后,体育设施不能发挥其
采用相空间重构和支持向量机相结合的方法建立混沌时间序列预测模型,用该模型对冷却剂体积流量进行预测。应用粒子群算法对模型中参数取值进行同步优化后,预测值与实际测量值的
近年来,随着社会经济的不断发展,我国的素质化教育也得到了不断地推广。当前,我国的体育事业发展较快,但在实践过程中仍然存在着思想政治教育工作上的问题,因此,在文化大发展