The thermodynamic conditions for dewetting of a liquid solder drop on copper thin films were examined under a hot-stage optical microscope in a flowing protective atmosphere.Dewetting of liquid solder was found to depend strongly on the copper film thickness and preceded by spalling of Cu 6 Sn 5 intermetallic compounds.However,the loss of interfacial bonding by spalling was not sufficient to cause immediate dewetting of solder drops if the wetting tip was still strongly bonded to the copper film.By introducing a pinning force on the wetting front,a sufficient condition was found from a force balance analysis for dewetting of the liquid solder drop,in general agreement with the experimental results.
The thermodynamic conditions for dewetting of a liquid solder drop on copper thin films were examined under a hot-stage optical microscope in a flowing protective atmosphere. Dewetting of liquid solder was found to depend strongly on the copper film thickness and preceded by spalling of Cu 6 Sn 5 intermetallic compounds. However, the loss of interfacial bonding by spalling was not sufficient to cause immediate dewetting of solder drops if the wetting tip was still strongly strongly bonded to the copper film. By introducing a pinning force on the wetting front, a sufficient condition was found from a force balance analysis for dewetting of the liquid solder drop, in general agreement with the experimental results.