Functionalized ionic liquids (FILs) as extractants were employed for the separation of tungsten and molybdenum from a sulfate solution for the first time. The effects of initial pH, extractant concentration, metal concentrations in the feed were comprehen
【机 构】
：
School of Resource and Civil Engineering,Northeastern University,Shenyang 110819,China;Zhengzhou Ins
论文部分内容阅读
Functionalized ionic liquids (FILs) as extractants were employed for the separation of tungsten and molybdenum from a sulfate solution for the first time. The effects of initial pH, extractant concentration, metal concentrations in the feed were comprehensively investig-ated. The results showed that tricaprylmethylammonium bis(2,4,4-trimethylpentyl)phosphinate ([A336][Cyanex272]) could selectively extract W over Mo at an initial pH value of 5.5; the best separation factor βW/Mo of 25.61 was obtained for a solution with low metal concentrations (WO3: 2.49 g/L, Mo: 1.04 g/L). The [A336][Cyanex272] system performed effectively for solutions of different W/Mo molar ratios and differ-ent metal ion concentrations in the feed. The chemical reaction between [A336][Cyanex272] and W followed the ion association mechanism, which was further proved by the Fourier-transform infrared (FTIR) spectra of loaded [A336][Cyanex272] and the free extractant. The strip-ping experiments indicated that 95.48％ W and 100.00％ Mo were stripped using a 0.20 mol/L sodium hydroxide solution. Finally, the select-ive extractions of W and Mo from two synthetic solutions of different high metal concentrations were obtained; the separation factor βW/Mo reached 23.24 and 17.59 for the first and second solutions, respectively. The results suggest the feasibility of [A336][Cyanex272] as an extract-ant for the separation of tungsten and molybdenum.
其他文献
All-solid-state Li-ion batteries (ASSLIBs) have been widely studied to achieve Li-ion batteries (LIBs) with high safety and energy density. Recent reviews and experimental papers have focused on methods that improve the ionic conductivity, stabilize the e
The microstructural evolution and performance of diamond/Al composites during thermal cycling has rarely been investigated. In the present work, the thermal stability of diamond/Al composites during thermal cycling for up to 200 cycles was explored. Speci
Wood-based panels containing urea-formaldehyde resin result in the long-term release of formaldehyde and threaten human health. In this study, inorganic aluminosilicate coatings prepared by combining metakaolin, silica fume, NaOH, and H2O were applied to
Silicon (Si) is widely considered to be the most attractive candidate anode material for use in next-generation high-energy-density lithium (Li)-ion batteries (LIBs) because it has a high theoretical gravimetric Li storage capacity, relatively low lithiat
In the past few years, the all-solid lithium battery has attracted worldwide attentions, the ionic conductivity of some all-solid lithium-ion batteries has reached 10−3–10−2 S/cm, indicating that the transport of lithium ions in solid electrolytes is no l
In order to study the effect of continuous casting process parameters on the shape of slab solidification end under non-uniform cooling, a solidification model of a continuous-cast slab with non-uniform cooling condition was established with ProCAST softw
The silicon-based material exhibits a high theoretical specific capacity and is one of the best anode for the next generation of ad-vanced lithium-ion batteries (LIBs). However, it is difficult for the silicon-based anode to form a stable solid-state inte
Anion-immobilized solid composite electrolytes (SCEs) are important to restrain the propagation of lithium dendrites for all solid-state lithium metal batteries (ASSLMBs). Herein, a novel SCEs based on metal-organic frameworks (MOFs, UiO-66-NH2) and super
An explosion-welded technology was induced to manufacture the GH3535/316H bimetallic plates to provide a more cost-effective structural material for ultrahigh temperature, molten salt thermal storage systems. The microstructure of the bonding interfaces w
Ultrafine nano-scale Cu2Sb alloy confined in a three-dimensional porous carbon was synthesized using NaCl template-assisted va-cuum freeze-drying followed by high-temperature sintering and was evaluated as an anode for sodium-ion batteries (SIBs) and pota