FePt (50 nm) and [FePt(a nm)/MgO(b nm)]5/glass (a=1, 2, 3; b=1, 2, 3) films were prepared by radio frequency (RF) magnetron sputtering technique, and then were annealed at 600°C for 30 min. The effect of MgO layer thickness on the structures and magn