WC- 10Co nanocomposite powder produced by spray pyrolysis-continuous reduction and carbonization technology was used, and the vacuum sintering plus sinterhip pr
【机 构】
：
State Key Laboratory of Advanced Technology for Materials Synthesis & Processing,Wuhan University of
论文部分内容阅读
WC- 10Co nanocomposite powder produced by spray pyrolysis-continuous reduction and carbonization technology was used, and the vacuum sintering plus sinterhip process was adopted to prepare ultrafine WCCo cemented carbide. The microstructure, grain size, porosity, density, Rockwell A hardness ( HRA ), transverse rupture strength (TRS), saturated magnetization and coercivity force were studied. The experimental results show that average grain size of the sample prepared by vacuum sintering plus sinterhip technology was about 420 nm, transverse rupture strength was more than 3460 MPa, and Rockwell A hardness of sintered specimen was more than 92.5. Ultrafine WC- 10Co cemented carbide with high strength and high hardness is obtained.
其他文献
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
高压变频器在昆钢炼铁厂废气引风机系统中的应用,能准确、方便、可靠地实现所需的控制方式,满足除尘工艺的要求,在提高自动化控制水平,节能降耗等方面具有较好的发展全景.
目的 探讨三磷酸腺苷(ATP)激活哺乳动物雷帕霉素靶蛋白(mTOR)/信号转录和转导激活因子3(STAT3)通路在脊髓损伤中的作用及其机制.方法 取80只健康成年雌性SD大鼠,体重250～300 g
目的 观察化疗药复合后对聚甲基丙烯酸甲酯(PMMA)骨水泥的理化性质的影响,探讨复合化疗药的PMMA骨水泥理化性能.方法 将甲氨蝶呤(MTX)、表阿霉素(EPI)进行75℃热处理10 rmin
目的观察单用二甲双胍血糖控制不佳的新诊断2型糖尿病患者加用沙格列汀降糖的有效性及安全性。方法2011年11至2012年9月选取180例新诊断的2型糖尿病患者(均为单用二甲双胍12周而血糖尚不达标)，按随机数字表法分为沙格列汀联合治疗(90例)与阿卡波糖联合治疗(90例)，随访12周，观察各项血糖指标变化，并记录不良反应发生情况。组间比较采用t检验，定性资料组间比较采用χ2检验。结果治疗12周后，沙
普通克里金方法具有空间结构探索及插值分析(给出插值结果及其精度)的功能.但是,绝大部分的克里金方法主要用于空间插值,在时空插值方面的研究还较少.综合考虑具体的实验区域
第四届全国癫痫学术会议纪要本届学术会议于１９９７年５月１８～２３日在湖南省张家界市召开。会议收到论文８４２篇，参加会议代表共３７２名。会议由中华神经科学会癫痫学组副组长沈鼎烈教授主持。会议采取大
目的 构建人的生物钟基因Period2 (hPer2)真核表达载体pEGFP-N1-hPer2,观察其在骨肉瘤细胞MG63中的表达.方法 应用实时定量荧光反转录聚合酶链反应(FQ-PCR)技术从MG63细胞中