The effect of surface morphology of 6H-SiC substrate on the ohmic contact properties of Ti/6H-SiC structure is studied. The H-terminated surface on Si-face 6H-SiC is obtained by both dipping SiC into HF acid solution for 15 s and thermal heating SiC in hydrogen atmosphere at 1100 C for 10 min, while the H-terminated surface on C-face 6H-SiC could be obtained only by the latter method. Ti is deposited on Si-face and C-face SiC substrates with H-terminated surfaces and ohmic contact is obtained without high-temperature annealing.
The effect of surface morphology of 6H-SiC substrate on the ohmic contact properties of Ti / 6H-SiC structure is studied. The H-terminated surface on Si-face 6H-SiC is obtained by both dipping SiC into HF acid solution for 15 s and thermal heating SiC in hydrogen atmosphere at 1100 C for 10 min, while the H-terminated surface on C-face 6H-SiC could be obtained only by the latter method. Ti is deposited on Si-face and C-face SiC substrates with H-terminated surfaces and ohmic contact is obtained without high-temperature annealing.