Sheets of aluminum 6061 alloy were welded using bypass-current double-sided arc welding with Al–Si filler wire to investigate the effect of Al–Si intermetallic compounds on the microstructure, microhardness and corrosion behavior of weld joint. Experimental results indicated that the Al_(4.5)FeSi phase in the topside of the weld joint was finer than that in the backside and newly formed phase of Al_(0.5)Fe_3Si_(0.5)was observed in the backside. The formation of reinforcing phases of Al–Fe–Si in the weld improved the microhardness of the weld by about 18%. The corrosion resistance of the weld zone was greater than that of the base metal, while the corrosion current displayed opposite, and the corrosion resistance of the weld region was better than that of the base metal.
Sheets of aluminum 6061 alloy were welded using bypass-current double-sided arc welding with Al-Si filler wire to investigate the effect of Al-Si intermetallic compounds on the microstructure, microhardness and corrosion behavior of weld joint. Experimental results indicated that the Al_ (4.5) FeSi phase in the topside of the weld joint was finer than that in the backside and newly formed phase of Al_ (0.5) Fe_3Si_ (0.5) was observed in the backside. The formation of reinforcing phases of Al-Fe-Si in the weld improved the microhardness of the weld by about 18%. The corrosion resistance of the weld zone was greater than that of the base metal, while the corrosion current displayed opposite, and the corrosion resistance of the weld region was better than that of the base metal.