【摘 要】
：
In the present work,the effects of trace element Sr on the microstructure,tensile properties,fractography and morphology of the eutectic Si of ZL114A (Al-7Si) c
【机 构】
：
College of Materials Science and Engineering, Chongqing University, Chongqing 400030, China;Baoji Pe
论文部分内容阅读
In the present work,the effects of trace element Sr on the microstructure,tensile properties,fractography and morphology of the eutectic Si of ZL114A (Al-7Si) cast alloy were investigated.The cast ZL114A aluminum alloy was prepared using a metal mold,and then heat treated with the T6 technique.The test results of mechanical properties show that modification element Sr can improve significantly the ultimate tensile strength,elongation and hardness of the ZL114A-T6 aluminum alloy.By adding 0.04％Sr,the values of the tensile strength Rm,elongation A and hardness HB increase from 230 MPa,1％ and 65 to the maximum of 305 MPa,8％,and 100,respectively.SEM analysis indicates that the near tensile fracture surface on longitudinal section of the ZL114A-T6 alloy reveals a transgranular fracture mode without Sr modification,while the tensile fracture is an intergranular fracture mode after Sr modification.The morphology of the eutectic Si phase is changed from acicular to fine fibrous.
其他文献
In this work,the influence of graphite on the ball-milled TiCx was studied.The results show that the lattice parameter of TiCx is increased when TiCx particles
By the end of July, ChinaPetroleum TechnologyDevelopment Company(CPTDC), one of CNPC’ssubsidiaries, has cumulativelysold 26 oil drilling rigs worthmore than U
伴热系统在油田集输系统中起着重要的作用,而伴热系统中的热水管线腐蚀现象给生产造成了巨大的影响,给国民经济带来了巨大的损失.华北油田留楚油田三管伴热集油流程中的伴热
香蕉西葫芦(Cucurbita pepo L.)是一种外形似香蕉、果皮为黄色的西葫芦,属葫芦科南瓜属一年生草本植物,是美洲南瓜中的一个黄色果皮新品种,以食用嫩果为主,嫩果肉质细嫩,味微
英语资源的选择,最关键的不是哪种资源好不好的问题,而是资源提供的时机和资源使用的方法问题。每一种资源都有它的功能,但是,也有它的局限。把各种资源有机地结合起来立体使
目的了解长春市中小学生乙肝感染情况,为防治工作提供科学依据。方法采取整群抽样方法,对2011-2012年长春市中小学新生体检工作中进行调查。结果长春市中小学生乙肝病毒的感
水平井钻井技术是利用特殊的井下动力钻具与随钻测量仪器,钻成井斜角大于86°,并保持这一角度钻进一定长度井段的定向钻井技术.在油气田开发中,水平井可以增加裸露出油面积,
The effect of Ti on the microstructure and mechanical properties of zinc-aluminum ZnAl4Y alloy has been investigated in this work.Small amount of Ti was added i