【摘 要】
：
用水(溶液)/AEO/环己烷/正戊醇的微乳体系,制备了分散性良好、尺寸均一的单斜结构CaSO_4·0．662H_2O纳米棒,其平均直径为50mm,长度为800～1600nm．研究表明,当水/表比(ω)为6～15、
【机 构】
：
上海大学化学系,上海大学化学系,上海大学化学系 上海 200436；安徽农业大学应用化学系,合肥 230036,上海 200436,上海 200436
论文部分内容阅读
用水(溶液)/AEO/环己烷/正戊醇的微乳体系,制备了分散性良好、尺寸均一的单斜结构CaSO_4·0．662H_2O纳米棒,其平均直径为50mm,长度为800～1600nm．研究表明,当水/表比(ω)为6～15、油/表比(γ)在5～12之间、反应物浓度为0．05～0．3mol/L时,适合于棒状硫酸钙的合成．性质研究发现,纳米硫酸钙在339nm处有较强的紫光发射,这在纳电子器件等领域有广阔的应用前景．
The monodisperse CaSO 4 · 0.662H 2 O nanorods with good dispersion and uniform size were prepared by microemulsion system of water / solution of AEO / cyclohexane / n-amyl alcohol with average diameter of 50mm and length of 800 ~ 1600nm . The results show that when the ratio of water / surface to the surface is 6-15 and the oil / surface ratio is between 5-12 and the reactant concentration is 0.05-0.3 mol / L, Synthesis. The nature of the study found that nano-calcium sulfate has a strong violet emission at 339nm, which has broad application prospects in the field of nanoelectronic devices.
其他文献
【摘 要】随着经济的不断增长，电力系统的负荷特性发生了很大的变化。为了了解地区负荷状况、把握其电力负荷特性的规律和发展趋势，本文根据某电网电力负荷情况、用电量情况，分析了此地区电力负荷特性，主要剖析了引起负荷特性变化的几个因素，论述了电力负荷的构成及其对电力负荷特性的影响，从而为开展电网建设、实现资源优化、发展经济等提供了理论依据。 【关键词】电力负荷 特性分析 电力负荷特性是我们现代化经济不
目的 探讨食管静脉曲张择期行内镜下静脉曲张套扎术(EVL)后早期再出血者的危险因素,并评估早期再出血者的远期预后.方法 对198例肝硬化合并食管静脉曲张择期行EVL二级预防患
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
采用二次电化学沉积法制备了聚苯胺-碲化铋复合纳米棒．首先在多孔氧化铝模板上电化学沉积聚苯胺纳米管,以导电聚苯胺纳米管作为二级模板,继续电化学沉积碲化铋,获得聚苯胺包裹
随着社会、科技、文化的进步，按键指纹锁已经越来越不能满足百姓的需求，智能触屏指纹锁应运而生。相比机械按钮，触摸屏更加智能便捷，只要用手指轻触就可以实现各种操作，更符合现代
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
采用醋酸钡和异丙醇钛为原料,邻苯二酚作钛醇盐的稳定剂,制备了BaTiO_3凝胶纤维；采用正己烷作溶剂,将BaTiO_3凝胶纤维在180℃条件下溶剂热处理12h；对预处理过的BaTiO_3纤维以1
11月19日到21日，“2014年中国五金·门窗年度产业峰会”在广东深圳隆重召开，国家部委领导、国内外五金行业的著名专家、学者、行业协会负责人，以及来自国内外的五金企业高管共聚
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥