The aging characteristic of Cu-0.6Cr-0.15Zr-0.05Mg-0.02Si alloy containing trace rare earth yttrium was investigated. The results showed that Cu-0.6Cr-0.15Zr-0.
This paper studies the influence of radial depth on vibration, chip formation and surface roughness during face milling of AISI304 austenitic stainless steel wi