采用旋转喷涂法在Si(100)基片上制备Ni0.25Zn0.15Fe2.6O4(100 nm)铁氧体薄膜作为种子层,然后在种子层上采用射频磁控溅射法沉积Ni0.25Cu0.09Zn0.66Fe1.998O4(600 nm)铁氧体薄膜。研究了种子层对NiZn铁氧体双层膜微观形貌、饱和磁化强度、矫顽力、磁导率及截止频率的影响。结果表明,Ni0.25Zn0.15Fe2.6O4种子层的引入促进了NiZn铁氧体双层膜尖晶石相的晶化和晶粒生长。NiZn铁氧体双层膜的饱和磁化强度Ms为420 kA/m,矫顽力Hc为5.