【摘 要】
：
In order to improve the quality of the bio-active coating on medical grade CoNiCrMo substrate, hydroxyapatite(HA) coatings were produced via low-temperature dip
【机 构】
：
College of Materials Science and Technology,Institute of Ceramic Materials
论文部分内容阅读
In order to improve the quality of the bio-active coating on medical grade CoNiCrMo substrate, hydroxyapatite(HA) coatings were produced via low-temperature dip-coating route on substrates treated using various surface pre-treating methods. The surface and cross-sectional morphologies of HA coatings were observed by SEM, as well as the bonding strength between coatings and substrates after different pre-treatments were characterized according to ASTM C633. The low-temperature HA dip-coating method with the substrate merely oxidized at 600℃ can provide a high quality HA coating for CoNiCrMo, of which the bonding strength reaches (58±5)MPa, higher than that of the clinically used HA coatings on Ti-alloys produced via plasma spray route, as well as a HA coating with full crystallinity and high phase-purity, which is more in-vivo stable than plasma sprayed HA coating.
其他文献
Various micro-mechanical and micro-structural influences on fatigue crack growth resistance of the material have been investigated over the years. It is widely
The reduction mechanism of stainless steelmaking dust and carbon pellets was investigated. The metal oxides present in the dust were reduced by carbon with a ne
SiCf/Ti-6Al-4V composites were fabricated by the powder-coated fiber method. The precursor fiber was prepared under the optimized parameter, and the composites
Mixture of green petroleum coke, B4C and SiC together with short carbon fiber were employed as starting materials, the mixture was press-formed without any bind
Sapphire crystals with different orientations may cone from implantation of Nb+ ions under different conditions and succedent annealing at reducing atmosphere.
Extraction of the Ligusticum Chuanxiong oil with supercritical CO2 (SC-CO2) was investigated at the temperatures ranging from 55℃ to 70℃ and pressure from 25
Network-induced delay and jitter are key factors causing performance degradation and instability of NCSs (networked control systems). The relationships between
The CCT curves of supercooled austenite were investigated by using THERMECMASTOR-Z simulation machine, test samples refined from 50 kg vacuum induction furnace
Si3 N4/TiC nanocomposite ceramics have been fabricated by hot pressing technique with Al2O3 and Y2O3 as additives.The results showed that well dispersed composi
The structure and disorder-order transformation of NdxFe60.5-xPt39.5(x = 0, 0.5, 1.0, 1.5) alloys were investigated in situ by high temperature X-ray diffractio