Superplastic tensile tests of AlNp/606l Al Composites, fabricated by powder metallurgy techniques, were performed at strain rates ranging from 10-1-10-3S-1 and at temperatures from 833 to 893 K. Hot rolling after extrusion was employed to obtain a fine gr