【摘 要】
：
本文研究了加热温度、保温时间、加热速度、冷却方式和形变度对GCr15钢退火组织和硬度的影响,定量测定了碳化物和晶粒尺寸。试验结果指出,亚温锻造退火新工艺细化晶粒尺寸,促
【机 构】
：
金属热处理教研室,金属热处理教研室,金属热处理教研室,
论文部分内容阅读
本文研究了加热温度、保温时间、加热速度、冷却方式和形变度对GCr15钢退火组织和硬度的影响,定量测定了碳化物和晶粒尺寸。试验结果指出,亚温锻造退火新工艺细化晶粒尺寸,促使碳化物球化和细化。形变温度越低,形变量越大,这种效果就越显著。对产生这种作用的原因进行了探讨,并提出了退火硬度公式,以说明退火硬度随加热温度的变化。
In this paper, the effects of heating temperature, holding time, heating rate, cooling method and deformation on the microstructure and hardness of GCr15 steel were investigated. The carbide and grain size were quantitatively determined. The experimental results show that the new technology for the sub-temperature forging annealing grain refinement size, to promote carbide ball and refinement. The lower the deformation temperature, the greater the amount of deformation, the more significant this effect. The reasons for this effect were discussed, and the annealing hardness formula was proposed to illustrate the change of annealing hardness with the heating temperature.
其他文献
This paper makes a comprehensive survey on power system blackout modeling and analysis based on SOC (self-organized criticality). Firstly,a generalized SOC theo
本文采用腐蚀实验、电化学测试及X光电子能谱(XPS)对不同成分的高纯铁素体不锈钢(F·S·S)在湿法磷酸中的耐蚀性及其耐蚀机理进行了研究。结果表明,铬是控制F·S·S耐蚀性的
强力航空发动机活塞的工作特点是承受着很大的机械负荷,活塞顶在高温下承受着高达8～10吨的气体压力,在润滑困难的情况下承受着巨大的侧压力和摩擦力。活塞的内腔较深,底部有
本文试验研究了GCr15钢冷模具原始组织经高温固溶碳化物细化予处理,再通过控制马氏体形态的低温短时加热淬火和奥氏体晶粒超细化的四次循环快速加热淬火;以及球化加常规工艺
液体静压轴承具有许多优点,它作为机床主轴的支承已有不少的应用实例,但是否能应用于高速内圆磨头呢?我厂通过试验和生产应用证明是完全可行的。一、问题的提出我厂生产的光
王朝向左,英雄向右。历史上从不缺乏有心杀贼、无力回天的悲情角色,无论是文臣文天祥还是武将袁崇焕,他们都无法凭一己之力阻止一个王朝的覆灭。这样的悲剧不仅仅是政治舞台
根据冶金学的观点,钢的强化因素有:(1)晶粒细化,(2)固溶强化;(3)析出强化;(4)相变强化;(5)加工强化;(6)珠光体强化等。对控制轧制(以下简称 CR)的钢而言,上述强化因素都能起
上文简单介绍了电阻应变式力传感器的工作原理,从中可以看出,弹性元件是传感器中将力P转换为应变ε的关键元件,电阻应变片是将应变ε变换为电阻值P变化的敏感元件。而整个测
随着足球的影响力越来越大,越来越多的非竞技因素逐渐渗入到足球当中,尤其在进入20世纪90年代后,世界杯中掺入例如娱乐、商业、权力甚至暴力等。这些因素的交锋让人眼花缭乱,
在我公司发动机批生产中,多次发现某些高温合金制造的零件,在工序间或最终热处理后,表面产生了腐蚀缺陷。腐蚀的形态多呈麻坑或虫蛀状。多次成批报废。 为找出产生腐蚀的原