The membranes of sulfonated poly(etheretherketone) with 65% sulfonation degree were prepared by doping of Y2O3 and ionic liquids,such as 1-ethyl-3-methylimidazol
【机 构】
:
School of Materials Science and Engineering,School of Wenling
【基金项目】
:
The authors are grateful to the National Natural Science Foundation of China;Postgraduate Innovation Fund of Shanghai University;教育部高等学校博士学科点专项科研基金
论文部分内容阅读
The membranes of sulfonated poly(etheretherketone) with 65% sulfonation degree were prepared by doping of Y2O3 and ionic liquids,such as 1-ethyl-3-methylimidazole tetrafluoroborate (EB) or 1-butyl-3-methylimidazole methanesulfonate (BS),respectively.And the properties,including conductivities,water uptake,thermal stability and mechanical properties,of pure SPEEK based proton exchange membrane and SPEEK based proton exchange membranes by doping of ionic liquids and Y2O3 have been studied in the present investigation.The experimental results showed that the conductivity of membranes increased with the temperature increased from 30 to 90 ℃,except for that of pure SPEEK membrane increased with increasing temperature from 30 to 70 ℃ and decreased with increasing temperature from 70 to 90 ℃.The conductivities of SPEEK/EB/Y2O3 and SPEEK/BS/Y2O3 composite membranes at 90 ℃ were 9.04 × 10-2 S cm-1 and 1.18 × 10-1 S cm-1 at 100% relative humidity (RH) and 8.04 × 10-2 S cm-1 and 1.02 × 10-1 S cm-1 at 50%RH,respectively.It has been also found that the water uptake and thermal stability of the membranes slightly improved by doping of ionic liquids and Y2O3.The tensile stress at break at room temperature was 2.61 MPa and 2.33 MPa,for SPEEK/EB/Y2O3 and SPEEK/BS/Y2O3,respectively.Therefore it may be considered that the modification with ionic liquids and Y2O3 is good potential method for improving the properties if SPEEK proton exchange memberane.
其他文献
In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare
Magnetic Co1-xNixFe2O4 nanoparticles (NPs) were successfully synthesized via a solvothermal method using ethylene glycol as solvent.The samples were characteriz
The solidification microstructure has an important effect on the mechanical properties of castings.Therefore,an FE (Finite Element) - CA (Cellular Automaton) co
Many years experience of the operation of high stress (>72% specified minimum yield strength,SMYS) gas pipelines and statistical analysis results of pipeline inci
Video accelerator is developed for better user experience in video sharing websites such as YouTube.PPLive video accelerator (PPVA),which has the largest number
PtSnNa/AlSBA-15 catalysts with different amounts of Sn were prepared for propane dehydrogenation.The catalysts were characterized by XRF,BET,H2 chemisorption,NH
A high accuracy frequency synchronization method is proposed for the 3rd generation partnership project (3GPP) long term evolution advanced (LTE-A) downlink rec
A novel moving objects segmentation method is proposed in this paper.A modified three dimensional recursive search (3DRS) algorithm is used in order to obtain m
The effect of cooling rate on plastic deformation of Zr-based bulk metallic glasses has been studied.The specimens with the diameters of 3 mm,4 mm and 6 mm cut