研究了熔体快淬法所得La0.85Sr0.15Mn合金经过氧化处理后的组织变化和磁阻特性,结果表明:(1)这一合金在大气中加热氧化处理,在较低温度下可得到具有钙钛矿结构的La0.85Sr0.15MnOy。(2)经过1073K以上温度的热处理后,所得材料的磁
The microstructures and magnetoresistance characteristics of La0.85Sr0.15Mn alloy obtained by the melt quenching method were investigated. The results show that: (1) The alloy is heated and oxidized in the atmosphere at low temperature, Perovskite structure of La0.85Sr0.15MnOy. (2) After the heat treatment at a temperature of 1073K or above, the resulting material is magnetically