PA6/PET bicomponent fiber at different spinning speeds were produced. Influences of cross blowing, spinning speed, PA6 and PET component ratio, drawing condition etc. on the mechanical properties, heat shrinkage, orientation and crystallization of the fiber were investigated. Also the rules among these influencing parameters were obtained. The splitting property of the fiber and its influence on the textile processing are discussed, which offers a base for the production of PA6/ PET bicomponent fiber using splitting technology. PA6 / PET bicomponent fiber at different spinning speeds were produced. Influences of cross blowing, spinning speed, PA6 and PET component ratio, drawing condition etc. on the mechanical properties, heat shrinkage, orientation and crystallization of the fiber were investigated. Also the rules among these influencing parameters were obtained. The splitting property of the fiber and its influence on the textile processing are discussed, which offers a base for the production of PA6 / PET bicomponent fiber using splitting technology.