论文部分内容阅读
摘要：防水防渗漏是地下人防工程施工中经常遇到的问题，特别是对于地处多水流域、地下水位较浅的相关工程，如不采取有效的施工工艺和技术措施，必然会导致地下工程出现局部或大部渗水现象，对结构安全和质量造成一定影响。本文结合某地下人防工程的施工经验，对防水施工技术进行探索和讨论，为同类工程施工提供一定借鉴。
关键词：人防工程，防水防渗漏 ，控制技术
Abstract: the underground waterproof and leakage is frequently encountered in the construction of civil air defense projects, especially for more water basin is located in underground water level, more shallow related projects, such as not take effective construction technology and technical measures, will lead to the underground engineering appear local or most ooze water phenomenon, safety and quality of structure caused by certain effect. This paper one of civil air defence works construction experience, waterproof construction technology to explore and discuss, for similar project construction to provide certain reference.
Keywords: human engineering, waterproof and seepage, and the control technology
中圖分类号：TU74文献标识码：A 文章编号：
1、前言
地下人防工程的质量在很大程度上取决于地下防水施工质量的效果，本工程根据结构防水的要求和所处的环境，对自防水混凝土、防水卷材的施工技术要点进行了分析，同时根据地下工程防水渗漏多出现的问题，特别是对各节点、细部及薄弱部位，提出了行之有效的质量控制措施。
2、工程概况
天津市塘沽区滨海新区中心商业区西沽还迁商品房地块二地下车库工程为新建地下一层核6常6人防汽车库，占地约26693㎡，为掘开式地下人防工程，外剪力墙墙，内框架结构形式。
结构防水设计为两道，分别为钢筋混凝土自防水和SBS改性沥青防水卷材一道，厚度4mm。主体混凝土抗压强度设计值均为C30，其中地下室外墙、底板及与室外土接触的顶板均采用防水砼，防水等级为2级，抗渗等级为S8。
3、防水施工方案
本项目防水形式为刚性防水和柔性防水相结合，刚性防水为砼C30，S8自防水，柔性防水为SBS改性沥青卷材4mm一道。
2.1自防水混凝土的施工
2.1.1钢筋模板施工
为提高结构的整体性，对底板钢筋、后浇带钢筋接头采用可靠连接，绑扎外墙钢筋时，严禁绑扎钢丝和墙体拉结钢筋接触模板，以免形成渗水通道。 除部分施工缝采用木模外，其余采用覆膜多层板。后浇带处模板采用钢管和预埋钢筋加固，其余部位采用对拉螺栓加固。
2.1.2 施工缝留置与处理
施工缝严格按照规范要求进行凿毛处理，然后将钢筋、塑料止水带用钢丝刷和湿布清理干净。安放BW止水条时，应用水泥钉固定牢固，其放置时间应严格掌握，在浇筑前严禁与水接触，以免泡水膨胀而失效，同时在浇筑前应先填与混凝土相同成分的水泥砂浆，使新旧混凝土紧密结合。
2.1.3 混凝土施工
混凝土使用低水化热的矿渣水泥，防止出现温度裂缝。浇筑采用斜面分层布料施工法，即一个坡度、分层浇筑、循序渐进、一次到顶的方法；外墙混凝土浇筑采用溜槽入模，对浇筑中出现的泌水，及时清除，混凝土采用1层塑料薄膜及2层草帘覆盖养护。
本工程设置了多道贯穿整个地下室的后浇带，这些部位是防水最薄弱点，后浇带混凝土采用C35，在后浇带两侧混凝土浇筑2个月以后开始浇筑。
2.2 SBS改性沥青防水卷材的施工
卷材防水层施工，分两步进行，第一步为底板及其立面范围内的防水层施工，第二步外墙及顶板范围内的防水层施工。第一步采用外防内贴法；第二步采用外防外贴法，防水卷材施工采用热熔法。
A、涂刷基层处理剂：在干燥的基层上涂刷基层处理剂，涂刷时必须涂刷均匀，操作迅速，不得漏刷，切勿反复涂刷。
B、卷材防水铺贴时，按位置把卷材两边卷曲，点燃喷灯，用喷灯加热基层和柔性油毡，加热时要均匀，喷灯距离卷材0.3米左右，待柔性油毡表面熔化后，缓慢地滚铺，卷材与基层粘结牢固，将气体顺次赶出，不得有窝气。
C、趁柔性油毡尚未冷却，用抹子将边封好，再用喷灯均匀细致地接好接缝。
D、构造要求：卷材长边塔接110mm，短边搭不小于160mm，且上下层错开300mm。
在质量上，要求卷材与基层、卷材与卷材的粘结牢固，不应有皱褶、翘边、脱层、滑动现象；卷材表面无损坏；接头及收边处理严密；地下室防水为特殊工序，施工中应进行监控，保留监控记录。
4、防水防渗漏控制技术
本工程常年处在地下水位范围内，根据地下工程防水渗漏问题多出现在混凝土施工阶段、后浇带、穿墙管道及埋件以及墙体防水施工质量等方面，本项目采取了以下技术措施：
4.1 混凝土施工阶段
内外墙模板加固所用对拉螺栓及穿墙套管均应加焊止水钢板，止水钢板与对拉丝杆连接部位必须双面满焊，焊缝须饱满。在混凝土达到设计强度的75％以上时，方可拆除模板。外墙混凝土浇筑应使混凝土从一侧开始逐渐向前推进，并在混凝土斜面上均匀布位振捣。
4.2后浇带防水防渗漏处理：
由于后浇带的砼属于二期砼与一期砼的交接处，是地下室防水功能中的薄弱部位，非常容易引起渗漏，应特别予以注意。为保证接缝严密，经筛选采用UEA作为外加剂配制补偿收缩砼，掺入量为水泥用量的15%，它可使砼产生0.04%～0.06%的膨胀率，能有效提高砼的抗压强度，并有利于其长期强度稳定发展。后浇带处的砼强度等级应比两侧先浇砼强度等级提高一级。后浇带混凝土浇筑前，将原后浇带两侧混凝土凿毛并剔去表面的松动石子和浮浆层，露出坚硬石子；并在浇筑前用清水充分湿润、冲洗。
后浇砼与两侧先浇混凝土的施工间隔一般至少为2个月，这期间两侧先浇砼的体积收缩变形已趋于稳定，后浇的补偿收缩砼在两侧先浇砼及钢筋的限制下因膨胀使砼内部密实，并与两侧先浇砼相接密实，成为整体的无缝结构，可有效地保证后浇带施工质量。
4.3 混凝土施工缝防渗漏措施
施工时在混凝土墙板中留置施工缝，如果处理不当，在施工缝的台阶处存在着混凝土不密实层，或者表面没有认真凿毛，存在着一些隔离层。较常见的问题有：1、凹缝槽内由于上部墙板支模过程中掉入垃圾，清除不干净而降低了墙板的抗渗能力；2、在采取预埋止水金属板的施工缝接头焊接不密实；对于形成凹凸形式施工缝的模板，当混凝土尚未达到一定强度时就急于拆模，造成了局部开裂、松动或撬损，破坏后又未经技术处理；3、安装墙模板时，在施工缝部位支撑不牢，封口不严密；浇筑过程中，施工缝处铺设的水泥砂浆漏浆严重，没有采取可靠的措施，振捣欠佳；4、在浇筑前没有在施工缝处铺一层水泥砂浆，使上下不能牢固粘结；5、有的墙体或底板，由于跑模漏浆，找平层达80～100mm，维修时采用注浆，在找平层范围，没有在混凝土基面上，造成假象的注浆，原施工缝渗水没有得到解决。。
防止措施：防水混凝土原则上不留或少留施工缝，同一后浇带分区底板混凝土应连续浇筑，不得留施工缝。最低水平施工缝距底板面应不小于200mm，距穿墙孔洞边缘不少于300mm，并避免设在墙板承受弯矩或剪力最大的部位。在混凝土墙板上留置的水平施工缝宜设置止水钢板、埋设膨胀止水条。在混凝土浇筑前，用水将施工缝处冲洗干净，并保持湿润，铺上一层与混凝土灰砂比相同的水泥砂浆或水泥素浆。
4.4 穿墙管道、预埋件防渗漏措施
穿墙管或预埋件不是在混凝土施工前预先留置，而是在防水砼浇筑完毕后才凿洞打孔，重新增设；施工时安装的管道和固定模板的螺栓无设置止水环或焊缝不严密；穿墙管或预埋件与混凝土拉触面不清洁，或有锈蚀层，导致穿墙管和砼不能很好粘结；穿墙管或预埋件与砼接触部位混凝土振捣不密实，出现蜂窝、麻面等现象；穿墙套管与穿墙管道之间未采用施工规范要求的防水材料封堵，或虽然采用了该材料，但做工粗糙。
防止措施：穿墙管及固定模板用的对拉螺栓必须在套管及螺栓上加焊止水环，必须满焊并确保严密，同时加强对焊缝的检查；预埋件埋设前要除锈，按要求固定牢固，埋设后加强保护，不得碰撞振动。为了使预埋件稳固，应采取预埋固定架方法。
4.5 防水卷材施工防渗漏措施
在主体结构实体验收后，将固定模板用的对拉螺栓周边混凝土凿成直径50mm、深25mm的外大内小的洞，在根部将对拉螺栓割除，再将所留空洞浇水洗净、湿润后，用防水砂浆塞实、抹平、压光。对模板接缝处的水泥渣用磨光机磨平，将外墙、塑料止水带表面水泥浆等杂物用铲刀和钢丝刷清理干净。在基层清理干净后，涂刷与卷材配套的基层处理剂，以增强卷材与基层的粘结力，24h后方可铺贴卷材。基层处理剂不得过早涂刷，以免沾染灰尘影响粘结效果。首先铺贴后浇带、阴阳角等处附加层，然后拆除底板侧面保护墙上最上面保护砖，将露出卷材接头清理干净，再从一侧开始自下而上垂直进行大面铺贴。铺贴过程中，一定要将卷材内空气赶净，以免造成空鼓起泡；同时在回填土方过程中避免对防水层造成破坏。
6、结束语
本项目通过对自防水混凝土、防水卷材施工控制，特別加强对混凝土施工阶段、后浇带、穿墙管道及埋件以及墙体防水施工质量等方面，采取有效技术控制措施，将发生渗漏的概率降到最小，受到各方的好评，取得了良好的社会效益和经济效果。
参考文献：
1、《地下工程防水技术规范》 GB50108-2001
2、《混凝土结构工程施工及验收规范》 GB50204-2002
3、《地下防水工程施工质量验收规范》 GB50208-2002
注：文章内所有公式及图表请以PDF形式查看。
关键词：人防工程，防水防渗漏 ，控制技术
Abstract: the underground waterproof and leakage is frequently encountered in the construction of civil air defense projects, especially for more water basin is located in underground water level, more shallow related projects, such as not take effective construction technology and technical measures, will lead to the underground engineering appear local or most ooze water phenomenon, safety and quality of structure caused by certain effect. This paper one of civil air defence works construction experience, waterproof construction technology to explore and discuss, for similar project construction to provide certain reference.
Keywords: human engineering, waterproof and seepage, and the control technology
中圖分类号：TU74文献标识码：A 文章编号：
1、前言
地下人防工程的质量在很大程度上取决于地下防水施工质量的效果，本工程根据结构防水的要求和所处的环境，对自防水混凝土、防水卷材的施工技术要点进行了分析，同时根据地下工程防水渗漏多出现的问题，特别是对各节点、细部及薄弱部位，提出了行之有效的质量控制措施。
2、工程概况
天津市塘沽区滨海新区中心商业区西沽还迁商品房地块二地下车库工程为新建地下一层核6常6人防汽车库，占地约26693㎡，为掘开式地下人防工程，外剪力墙墙，内框架结构形式。
结构防水设计为两道，分别为钢筋混凝土自防水和SBS改性沥青防水卷材一道，厚度4mm。主体混凝土抗压强度设计值均为C30，其中地下室外墙、底板及与室外土接触的顶板均采用防水砼，防水等级为2级，抗渗等级为S8。
3、防水施工方案
本项目防水形式为刚性防水和柔性防水相结合，刚性防水为砼C30，S8自防水，柔性防水为SBS改性沥青卷材4mm一道。
2.1自防水混凝土的施工
2.1.1钢筋模板施工
为提高结构的整体性，对底板钢筋、后浇带钢筋接头采用可靠连接，绑扎外墙钢筋时，严禁绑扎钢丝和墙体拉结钢筋接触模板，以免形成渗水通道。 除部分施工缝采用木模外，其余采用覆膜多层板。后浇带处模板采用钢管和预埋钢筋加固，其余部位采用对拉螺栓加固。
2.1.2 施工缝留置与处理
施工缝严格按照规范要求进行凿毛处理，然后将钢筋、塑料止水带用钢丝刷和湿布清理干净。安放BW止水条时，应用水泥钉固定牢固，其放置时间应严格掌握，在浇筑前严禁与水接触，以免泡水膨胀而失效，同时在浇筑前应先填与混凝土相同成分的水泥砂浆，使新旧混凝土紧密结合。
2.1.3 混凝土施工
混凝土使用低水化热的矿渣水泥，防止出现温度裂缝。浇筑采用斜面分层布料施工法，即一个坡度、分层浇筑、循序渐进、一次到顶的方法；外墙混凝土浇筑采用溜槽入模，对浇筑中出现的泌水，及时清除，混凝土采用1层塑料薄膜及2层草帘覆盖养护。
本工程设置了多道贯穿整个地下室的后浇带，这些部位是防水最薄弱点，后浇带混凝土采用C35，在后浇带两侧混凝土浇筑2个月以后开始浇筑。
2.2 SBS改性沥青防水卷材的施工
卷材防水层施工，分两步进行，第一步为底板及其立面范围内的防水层施工，第二步外墙及顶板范围内的防水层施工。第一步采用外防内贴法；第二步采用外防外贴法，防水卷材施工采用热熔法。
A、涂刷基层处理剂：在干燥的基层上涂刷基层处理剂，涂刷时必须涂刷均匀，操作迅速，不得漏刷，切勿反复涂刷。
B、卷材防水铺贴时，按位置把卷材两边卷曲，点燃喷灯，用喷灯加热基层和柔性油毡，加热时要均匀，喷灯距离卷材0.3米左右，待柔性油毡表面熔化后，缓慢地滚铺，卷材与基层粘结牢固，将气体顺次赶出，不得有窝气。
C、趁柔性油毡尚未冷却，用抹子将边封好，再用喷灯均匀细致地接好接缝。
D、构造要求：卷材长边塔接110mm，短边搭不小于160mm，且上下层错开300mm。
在质量上，要求卷材与基层、卷材与卷材的粘结牢固，不应有皱褶、翘边、脱层、滑动现象；卷材表面无损坏；接头及收边处理严密；地下室防水为特殊工序，施工中应进行监控，保留监控记录。
4、防水防渗漏控制技术
本工程常年处在地下水位范围内，根据地下工程防水渗漏问题多出现在混凝土施工阶段、后浇带、穿墙管道及埋件以及墙体防水施工质量等方面，本项目采取了以下技术措施：
4.1 混凝土施工阶段
内外墙模板加固所用对拉螺栓及穿墙套管均应加焊止水钢板，止水钢板与对拉丝杆连接部位必须双面满焊，焊缝须饱满。在混凝土达到设计强度的75％以上时，方可拆除模板。外墙混凝土浇筑应使混凝土从一侧开始逐渐向前推进，并在混凝土斜面上均匀布位振捣。
4.2后浇带防水防渗漏处理：
由于后浇带的砼属于二期砼与一期砼的交接处，是地下室防水功能中的薄弱部位，非常容易引起渗漏，应特别予以注意。为保证接缝严密，经筛选采用UEA作为外加剂配制补偿收缩砼，掺入量为水泥用量的15%，它可使砼产生0.04%～0.06%的膨胀率，能有效提高砼的抗压强度，并有利于其长期强度稳定发展。后浇带处的砼强度等级应比两侧先浇砼强度等级提高一级。后浇带混凝土浇筑前，将原后浇带两侧混凝土凿毛并剔去表面的松动石子和浮浆层，露出坚硬石子；并在浇筑前用清水充分湿润、冲洗。
后浇砼与两侧先浇混凝土的施工间隔一般至少为2个月，这期间两侧先浇砼的体积收缩变形已趋于稳定，后浇的补偿收缩砼在两侧先浇砼及钢筋的限制下因膨胀使砼内部密实，并与两侧先浇砼相接密实，成为整体的无缝结构，可有效地保证后浇带施工质量。
4.3 混凝土施工缝防渗漏措施
施工时在混凝土墙板中留置施工缝，如果处理不当，在施工缝的台阶处存在着混凝土不密实层，或者表面没有认真凿毛，存在着一些隔离层。较常见的问题有：1、凹缝槽内由于上部墙板支模过程中掉入垃圾，清除不干净而降低了墙板的抗渗能力；2、在采取预埋止水金属板的施工缝接头焊接不密实；对于形成凹凸形式施工缝的模板，当混凝土尚未达到一定强度时就急于拆模，造成了局部开裂、松动或撬损，破坏后又未经技术处理；3、安装墙模板时，在施工缝部位支撑不牢，封口不严密；浇筑过程中，施工缝处铺设的水泥砂浆漏浆严重，没有采取可靠的措施，振捣欠佳；4、在浇筑前没有在施工缝处铺一层水泥砂浆，使上下不能牢固粘结；5、有的墙体或底板，由于跑模漏浆，找平层达80～100mm，维修时采用注浆，在找平层范围，没有在混凝土基面上，造成假象的注浆，原施工缝渗水没有得到解决。。
防止措施：防水混凝土原则上不留或少留施工缝，同一后浇带分区底板混凝土应连续浇筑，不得留施工缝。最低水平施工缝距底板面应不小于200mm，距穿墙孔洞边缘不少于300mm，并避免设在墙板承受弯矩或剪力最大的部位。在混凝土墙板上留置的水平施工缝宜设置止水钢板、埋设膨胀止水条。在混凝土浇筑前，用水将施工缝处冲洗干净，并保持湿润，铺上一层与混凝土灰砂比相同的水泥砂浆或水泥素浆。
4.4 穿墙管道、预埋件防渗漏措施
穿墙管或预埋件不是在混凝土施工前预先留置，而是在防水砼浇筑完毕后才凿洞打孔，重新增设；施工时安装的管道和固定模板的螺栓无设置止水环或焊缝不严密；穿墙管或预埋件与混凝土拉触面不清洁，或有锈蚀层，导致穿墙管和砼不能很好粘结；穿墙管或预埋件与砼接触部位混凝土振捣不密实，出现蜂窝、麻面等现象；穿墙套管与穿墙管道之间未采用施工规范要求的防水材料封堵，或虽然采用了该材料，但做工粗糙。
防止措施：穿墙管及固定模板用的对拉螺栓必须在套管及螺栓上加焊止水环，必须满焊并确保严密，同时加强对焊缝的检查；预埋件埋设前要除锈，按要求固定牢固，埋设后加强保护，不得碰撞振动。为了使预埋件稳固，应采取预埋固定架方法。
4.5 防水卷材施工防渗漏措施
在主体结构实体验收后，将固定模板用的对拉螺栓周边混凝土凿成直径50mm、深25mm的外大内小的洞，在根部将对拉螺栓割除，再将所留空洞浇水洗净、湿润后，用防水砂浆塞实、抹平、压光。对模板接缝处的水泥渣用磨光机磨平，将外墙、塑料止水带表面水泥浆等杂物用铲刀和钢丝刷清理干净。在基层清理干净后，涂刷与卷材配套的基层处理剂，以增强卷材与基层的粘结力，24h后方可铺贴卷材。基层处理剂不得过早涂刷，以免沾染灰尘影响粘结效果。首先铺贴后浇带、阴阳角等处附加层，然后拆除底板侧面保护墙上最上面保护砖，将露出卷材接头清理干净，再从一侧开始自下而上垂直进行大面铺贴。铺贴过程中，一定要将卷材内空气赶净，以免造成空鼓起泡；同时在回填土方过程中避免对防水层造成破坏。
6、结束语
本项目通过对自防水混凝土、防水卷材施工控制，特別加强对混凝土施工阶段、后浇带、穿墙管道及埋件以及墙体防水施工质量等方面，采取有效技术控制措施，将发生渗漏的概率降到最小，受到各方的好评，取得了良好的社会效益和经济效果。
参考文献：
1、《地下工程防水技术规范》 GB50108-2001
2、《混凝土结构工程施工及验收规范》 GB50204-2002
3、《地下防水工程施工质量验收规范》 GB50208-2002
注：文章内所有公式及图表请以PDF形式查看。