The thermoluminescence (TL) and photoluminescence (PL) properties of the phosphor NaSrBO 3 :Tb 3+ were reported and discussed. The combustion technique was used for the synthesis of polycrystalline samples of NaSrBO 3 :Tb 3+ . The TL glow curve of the compound had a simple structure with a single peak at 434 K. TL sensitivity of the phosphor was found to be more than that of (LiF:Mg,Cu,P). The TL glow curve was studied as a function of concentration of dopant and dose of gamma ray irradiation. The kinetic parameters of the thermoluminescence of NaSrBO 3 : Tb 3+ were calculated employing the peak shape method. The photoluminescence (PL) properties of Tb 3+ doped in NaSrBO 3 were studied over the 200-400 nm excitation range. The excitation spectra of NaSrBO 3 :Tb 3+ consisted of single narrow band peaking at about 236 nm. The emission spectra monitored at 236 nm excitation consisted of a series of sharp lines peaking at 489, 544, 586 and 622 nm corresponding to the 5 D 4 → 7 F j (j=3,4,5,6) transitions within the 4f 8 configurations of Tb 3+ .
The thermoluminescence (TL) and photoluminescence (PL) properties of the phosphor NaSrBO 3: Tb 3+ were reported and discussed. The combustion technique was used for the synthesis of polycrystalline samples of NaSrBO 3: Tb 3+. The TL glow curve of the compound had a simple structure with a single peak at 434 K. TL sensitivity of the phosphor was found to be more than that of (LiF: Mg, Cu, P). The TL glow curve was studied as a function of concentration of dopant and The kinetic parameters of the thermoluminescence of NaSrBO 3: Tb 3+ were calculated employing the peak shape method. The photoluminescence (PL) properties of Tb 3+ doped in NaSrBO 3 were studied over the 200-400 nm excitation range. The excitation spectra of NaSrBO 3: Tb 3+ consisted of single narrow band peaking at about 236 nm. The emission spectra monitored at 236 nm excitation consisted of a series of sharp lines peaking at 489, 544, 586 and 622 nm corresponding to the 5 D 4 → 7 F j (j = 3, 4 , 5,6) transitions within the 4f 8 configurations of Tb 3+.