采用真空感应和真空自耗双真空(VIM+ VAR)冶炼工艺生产的HGCr15 轴承钢,其中氧含量仅为(5 ~7) ×10- 6 。电渣钢ZGCr15 的氧化物夹杂含量是双真空HGCr15 轴承钢的4-2 倍。经真空热处理后轴承零件(HGCr15) 表面可以获得压应力。双真空HGCr15 的接触疲劳寿命L10是电渣钢的1-49 倍,断裂韧度KIC提高19% 。
The HGCr15 bearing steel produced by vacuum induction and vacuum consumable double vacuum (VIM + VAR) smelting process has an oxygen content of only (5 ~ 7) × 10 -6. Electrochemical slag ZGCr15 oxide inclusions content is double vacuum HGCr15 bearing steel 4-2 times. After vacuum heat treatment bearing parts (HGCr15) surface can get compressive stress. The contact vacuum life H10 of double vacuum HGCr15 is 1-49 times that of electroslag, and the fracture toughness KIC increases by 19%.