The microstructure of Ti-33wt-% Al-(1.6-4.5)wt-% Mn alloys are composed ofγ+α<sub>2</sub> phases,but the volume of x<sub>2</sub>-phase is a little.Mn alloying decreases the latticeparameters a and c of γ-phase and the c/a ratio bec